Trans. Nonferrous Met. Soc. China 25(2015) 3240−3246 Effect of indentation size and grain/sub-grain size on microhardness of high purity tungsten Guang-yu LIU, Song NI, Min SONG State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China Received 29 January 2015; accepted 13 May 2015 Abstract: Hardness of materials depends significantly on the indentation size and grain/sub-grain size via microindentation and nanoindentation tests of high-purity tungsten with different structures. The grain boundary effect and indentation size effect were explored. The indentation hardness was fitted using the Nix−Gao model by considering the scaling factor. The results show that the scaling factor is barely correlated with the grain/sub-grain size. The interaction between the plastically deformed zone (PDZ) boundary and the grain/sub-grain boundary is believed to be the reason that leads to an increase of the measured hardness at the specific depths. Results also indicate that the area of the PDZ is barely correlated with the grain/sub-grain size, and the indentation hardness starts to stabilize once the PDZ expands to the dimension of an individual grain/sub-grain. Key words: high purity tungsten; indentation hardness; indentation size effect; grain boundary; plastic deformation zone where H is the real hardness, Ho is generally called the 1 Introduction macroscopic hardness, corresponding to the hardness that results from statistica