熔体渗透参数对钨丝增强（Cu50Zn43Al7）99.5Si0.5非晶复合材料显微组织和力学性能的影响.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 2624−2629 Effect of melt infiltration parameters on microstructure and mechanical properties of tungsten wire reinforced (Cu Zr Al ) Si metallic glass matrix composite 50 43 7 99.5 0.5 1 2 1 Ebrahim Karimi SAEIDABADI , Reza GHOLAMIPOUR , Behrouz GHASEMI 1. Department of Materials and Metallurgical Engineering, University of Semnan, Semnan 35131-19111, Iran; 2. Iranian Research Organization for Science and Technology (IROST), Tehran 33531-36846, Iran Received 9 September 2014; accepted 4 February 2015 Abstract: Using melt infiltration casting at different temperatures (965, 990 and 1015 °C) for different time (10 and 15 min), the composites of (Cu Zr Al ) Si bulk metallic glass reinforced with tungsten wires were produced. X-ray diffraction (XRD), 50 43 7 99.5 0.5 scanning electron microscopy (SEM) and quasi-static compression tests were carried out to evaluate the microstructure and mechanical properties. The results show that the maximum ultimate compressive strength and strain-to-failure of about 1880 MPa and 16.7% were achieved, respectively, at the infiltration temperature of 965 °C for 15 min. Key words: Cu-based bulk metallic glass matrix composite; melt infiltration; shear band; tungsten wire the microstructure and mechanical properties of the 1 Introduction