StudyofPipelineSteelswithAcicularFerriteMicrostructure.pdfVIP

Materials Research . 2015; 18(1): 36-41 © 2015 DOI: /10.1590/1516-1439.256813 Study of Pipeline Steels with Acicular Ferrite Microstructure and Ferrite-bainite Dual-phase Microstructure a a Xiurong Zuo *, Zhengyue Zhou aSchool of Physics and Engineering, Zhengzhou University, Zhengzhou, 450052, PR, China Received: December 11, 2013; Revised: January 11, 2015 Three kinds of X70 steels with the same chemical composition and different microstructures fabricated by varying processes were compared in aspect of the microstructures and mechanical properties using SEM, TEM and tensile testing machine. The experimental results showed that the steel 1 with acicular ferritic microstructure fabricated by thermal-mechanical processing with online accelerated cooling (TMCP) exhibited an excellent combination of strength and toughness, but provided high yield ratio of 0.85, low uniform elongation of 8.3% as well as low strain hardening exponent of 0.09, indicating poor deformability. In contrast to above steel 1, the steel 2 and steel 3 having ferrite- bainite dual-phase microstructure respectively fabricated by TMCP and intercritical annealing exhibited the improved deformability in terms of the low yield ratio of 0.69 and 0.68, high uniform elongation of 12.8% and 11.8%, and strain hardening exponent of 0.157 and 0.155. It is argued that the optimum properties combination of strength, toughness and deformability can best be achieved by o