RH 喷粉快速脱碳技术研究 王晓峰 唐复平 王军 林洋 吴春杰 王小善 (鞍钢集团公司，鞍山，114014) 摘要 文提出一种全新的RH 脱碳精炼技术——RH 喷粉快速脱碳（RH-AS ），并开展了工业现场试验研究，分析了RH-AS 技术脱碳原理，考察了RH-AS 技术对钢水洁净度的影响。结果表明，采用RH-AS 喷粉脱碳技术能够进行脱碳处理，并且这 种技术在不改变现行工艺的条件下能够加速脱碳反应，缩短 RH 精炼处理时间至少 3min，吨钢成本降低 3～5RMB 。采用 RH-AS 技术处理后，铸坯的平均T[O]可达10ppm ，显著提高钢水的洁净度。RH-AS 技术值得深入研究、推广。 关键词 RH 脱碳 超低碳钢 碳酸钙 二氧化碳 小气泡 Development of a novel RH degassing process with powder injection through the nozzles of snorkel Wang Xiaofeng, Tang Fuping, Wang Jun, Lin Yang, Wu Chunjie, Wang Xiaoshan (Ansteel Group Corporation, Anshan, 114021，China) Abstract a novel decarburization process in RH degassing vacuum (named as RH-AS) has been put forward and the plant trials have been carried out and the ruling factors of the decarburization process of RH-AS have been analyzed. The results indicate that decarburization reaction can take place after RH-AS treatment and decarburization process can be accelerated, which results in the decarburization period shortening for at least 3min. Enlargement of interfacial area was considered to be the main decarburization mechanism.It is worth further studying RH-AS. Key words RH Decarburization Ultra-low carbon steel Calcium carbonate CO2 fine bubble 1 前言 超低碳钢以其优良的范性、韧性、加工性能和电磁性能等广泛地应用在各个领域。随着科学和技术的 发展，对许多钢的碳含量的要求越来越低，如IF 钢、显像管框架钢等要求真空脱碳能达到20ppm 以下， [1-2] 有的甚至要求小于 6ppm，才能使最终成品碳满足要求 。为了满足连铸生产节奏的要求，RH 真空处理 的时间必须限制在一定的范围之内。另外，缩短脱碳时间还可以减少RH 处理所需的钢水过热度，降低运 行费用。因此，提高脱碳速度和降低最终碳含量一直成为人们研究的对象。 采用普通的BOF-RH-CC 工艺生产超低碳钢存在的主要问题是：在RH 内要想达到理想的碳浓度所需 的时间太长，因此，为了缩短在RH 内的脱碳时间，必须降低转炉出钢时的碳浓度，但是，随之而来的是 钢水过分氧化和渣中(FeO)的增加，这对冷轧薄板的表面质量有不利影响。 [3-5] 促进脱碳研究可从以下两方面进行：⑴增大环流量；⑵体积传质系数 。增大环流量的有效措施有扩