核废料固化桶用钢纤维活性粉末混凝土性能研究.pdfVIP

学兔兔 2011年第4期 混凝 土 与 水 泥 制 品 201l No4 4月 CHINA CONCRETE AND CEMENT PRODUCTS April 核废料固化桶用钢纤维活性粉末混凝土性能研究 江晓君 ，严 云1,2，胡志华1,2 (1．西南科技大学材料学院，绵阳，621010；2．四川省先进建筑材料实验室，绵阳621010) 摘 要：高强高韧的纤维活性粉末混凝土(RPC)作为核废料固化桶的原材料具有很好的发展前景。为改善RPC 韧性较差的缺点，研究了钢纤维掺量对RPC力学性能及弯曲韧性性能的影响。试验结果表明．钢纤维的加入能够大 大提高RPC的力学性能及弯曲韧性，使RpC能更好地满足核废料固化桶材料的要求 关键词：核废料固化桶；RPC(活性粉末混凝土)；弯曲韧性；抗压强度；抗折强度 Abstract：As one raw material of container for storage of radioactive wastes，fiber reinforced high—strength and high— toughhess reactive powder concrete (RPC)has a good prospect．To improve the shortcoming of bad toughness of RPC，the effects of steel fiber dosage on the mechanical performances and flexural toughness are researched．The experimental results indicate that the mechanical performances and flexural toughness of RPC can be enhanced greatly by adding the steel fiber，which makes RPC satisfy the requirement of container for storage of radioactive wastes better． Keyword：Container for storage of radioactive wastes；RPC (Reactive Powder Concrete)；Flexural toughness； Compressive strength；Flexural strength 中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2011)04—50一O4 0 前言 用。 近20年来．我国的核电事业飞速发展．有力地 本文通过掺入钢纤维的方式来改善RPC的韧 推动了我国的建设事业．但同时也产生了大量的核 性，试验研究了钢纤维掺量对RPC力学性能及弯曲 废料．这些核废料若处置不当就会对环境和人体健 韧性的影响，使其能满足核废料固化桶对混凝土材 康造成很大危害f11。 料的性能要求。 核废料固化桶是处理中低放射性核废料的常 1 原材料及测试方法 用方式。因为核废料具有强放射性的特点，我国现 1．1 原材料 行标准EJ914—2002(低、中水平放射性固体废物混 (1)水泥 凝土容器》规定：固化桶