Al2O3TiCCaF2自润滑陶瓷材料的研究.PDF

Al O / T iC/ CaF 37 2 3 2 Al2 O3 / Ti C/ CaF2 Study on Self-lubricating Al O / T iC/ CaF Ceramic Composites 2 3 2 , , ( , 25 61) CAO T ong-kun, DENG Jian- xin, SU N Jun-long ( Department of Mechanical Engineering, Shandong University, Jinan 25 61, China) : Al O / T iC/ CaF , , CaF 1 % ( 2 3 2 2 , ) , Al O / TiC/ CaF , 589MPa H V 1537 2 3 2 , Al O / TiC/ CaF , , Al O / 2 3 2 2 3 TiC/ CaF , CaF 1 % , , 1 28 2 2 , CaF 15% , . 32 , Al O / TiC/ CaF 2 2 3 2 , , : ; ; ; : T Q174.758 : A : 1 1-4381( 2 5) 3- 37- 3 Abstract: T he Al2 O3/ TiC/ CaF2 self-lubricating ceramic composites w ere produced by means of hot- pressing . M echanical properties and microstructure w ere analyzed. It was found that the Al2 O3/ TiC with 1 % ( mass fraction, the same below) CaF2 had the highest hardness, HV 1537, and bending strength, 589MPa. Friction and w ear properties of the ceramic composites w ere investigated at room temperature. It w as found that the Al2 O3/ T iC w ith 1 % CaF2 had the low est friction coefficient, a- 2 3 2 bout . 28, w hile th