内浇口出流速度对大型铸钢件外观质量的影响.pdfVIP

学兔兔 内浇口出流速度对大型铸钢件外观质量的影响 潘凤英，马文治，刘亮亮，张 婧 (宁夏共享铸钢有限公司，宁夏 银川 750021) 摘要：大型铸钢件几乎都采用漏包浇注，铸件外观质量受到内浇口出流速度、浇注温度等浇注 参数的影响。分析了内浇口出流速度对铸钢件外观缺陷的影响因素，确定了最佳内浇口出流速 度，并运用到实际生产以改善铸钢件外观质量。 关键词：大型铸钢件；浇注系统；内浇口出流速度；外观缺陷 中图分类号：TG244 ．4 文献标识码：A 文章编号：1673—3320(2013)02—0023—03 Influence of Ingate Outflow Velocity on Appearance Quality of Large Steel Castings Pan Fengying，Ma Wenzhi，Liu Liangliang，Zhang Jing (Kocel Steel Found~Co．，Ltd．，Yinchuan 750021，Ningxia，China) Abstract：The bosom pouting ladle is almost used in pouring large steel castings．The appearance quality of castings is affected by pouring parameters，such as ingate outflow velocity,pouring temperature，etc． The influencing factors of ingate outflow velocity on appearance defects of steel castings were analyzed． The optimum ingate outflow velocity was determined，which is applied in practical production to improve the appearance quality of steel castings． Key words：large steel casting；gating system；ingate outflow velocity；appearance defect 浇注系统的设计是铸钢件铸造工艺设计中的 浇注系统内浇口出流速度y内：单位时间流入 一 个非常重要的环节，直接影响到铸件的内在和 型腔的金属液体积／浇注系统内浇口总截面积。 外在质量。对于铸钢件，特别是大型铸钢件 (一 该速度直接决定了钢液在型腔内的运动状态以及 般单件净重5 t以上)几乎都是漏包浇注，不必 对型腔壁的冲刷情况，其综合作用影响到铸钢件 像铸铁件一样要充分考虑集渣、孕育等方面的功 的品质。本文以生产的铸钢件产品为研究对象， 能，因此工艺人员在设计时往往忽视了其浇注系 针对铸件易出现的夹渣、粘砂等典型缺陷，从浇 统的作用。事实上，由于铸钢件浇注温度高，浇 注系统内浇口出流速度对铸钢件外部质量的影响 注过程中型腔表面受到钢液的热辐射后发生体积 进行研究，寻找出内浇口出流速度的最佳实施标 膨胀，其表层与内层分离进入钢液导致砂眼、气 准。 孔的产生；同时，在相对较高的浇注温度下，钢 液产生二次氧化，易在铸钢件内部形成夹杂；而 1 内浇口出流速度与铸钢件外观缺 且钢液的体收缩量大，浇注结束后必须营造良好 陷的关系 的温度梯度，以实现顺序凝固。浇注系统的各种 内浇口出流速度过小，随着铸钢件浇注质量 参数，包括内浇口出流速度、浇注时间、