大型铸钢件造型和制芯工艺的选用.pdfVIP

学兔兔 大型铸钢件造型和制芯工艺的选用 苏见波，张景超，李岩岩 (机械工业第六设计研究院有限公司，河南 郑州 450007) 摘要：简述了大型铸钢件造型和制芯工艺的现状，着重分析了碱性酚醛树脂砂、呋喃树脂砂和 酯硬化水玻璃砂的造型工艺特点，从型砂配比、硬化性能、型砂性能、铸件质量、旧砂回用、 劳动环保、经济评价和工艺评价等方面对三种型砂工艺进行了对比，为生产大型铸钢件时自硬 砂造型和制芯工艺的选择提供参考。 关键词：大型铸钢件；造型工艺；自硬砂 中图分类号：TG221 ．2 文献标识码：A 文章编号：1 673-3320(2014)04-001 1-04 Selection of Molding and Core Making Process for Large Steel Castings SU Jianbo，ZHANG Jingchao，LI Yanyan (SIPPR Engineering Group Co．，Ltd．，Zhengzhou 450007，Henan，China) Abstract：The present situation of molding and core making process for large steel castings was described briefly．The molding process characteristics of alkaline phenolic resin sand，furan resin sand and ester cured sodium silicate sand was analyzed emphatically．Three kinds of molding sand process were compared from molding sand ratio，hardening performance，sand performance，casting quality， sand recycling，environmental protection，economic evaluation and process evaluation，which provides the reference for a choice of molding and core making process with self-hardening sand in production of large steel castings． Key words：large steel castings；molding process；self-hardening sand 随着装备制造业的持续发展，我国铸造业保 总和，部分铸钢企业的技术和装备水平已经接近 持了良好的发展势头，在铸件产量连续增长的同 或达到世界一流水平【2_。中国一重铸钢件单重达 时，铸造技术水平也有了大幅度的提升。目前， 480 t，中国二重铸钢件单重达500 t，上海重机铸 我国已经能自主生产核电设备中的不锈钢主泵泵 钢件单重达453 t，大连重工铸钢件单重达200 t， 体、汽轮机缸体，水电机组的转轮、叶片、上 宁夏共享铸钢件单重达100 t。 冠、下环，火电机组中的汽缸体件，大型冶金设 大型铸钢件的制造质量将直接关系到国家重 备中的轧机机架、轧辊、大型轴承座等质量要求 点工程项目的质量、安全及进度，因此，提高大 高、技术复杂的大型铸钢件。大型铸钢件的制造 型铸钢件的铸造水平具有极大的现实意义和实用 业是国家装备制造的基础行业，其发展水平是衡 价值 。随着国家电力、冶金、矿山、船舶、石