铸铁件中白口缺陷的产生与防止.pdf

学兔兔 Dec。2008 ·l312· VO1．57 NO．12 铸铁件中白口缺陷的产生与防止 辜祖勋 (中国第一汽车集团铸造有限公司，吉林长春130062) 摘要：为解决铸件的自口问题，从铁碳平衡图和合金结晶凝固原理出发，分析了化学成分、过冷度、合金元素、铸型 介质、炉料等对产生白口的影响，结合生产实践经验，分析渗碳体的成因，提出相应地预防和消除的措施。并分析了 孕育处理对铸铁材质的影响。 关键词：白口；渗碳体；过冷；结晶核心 中图分类号：TG245 文献标识码：B 文章编号：1001-4977(2008)12—1312—04 Chilling Defect in IrOn Castings and Its Elimination GU ZU．xun (FAW Foundry Co．Ltd．，Changchun 130062，Jilin，China) Abstract：I n order to solve the problem of chill in castings，effect of such aspects as the chem ical composition，degree of supercooling，alloying element，mould material，charge and SO on were analyzed on the basis of iron-carbon diagram and alloys crystal and solidifying principle．The reason of cementite formation was analyzed based on productive practice and the measures of preventing and eliminating the chill were put forward．The effect of inoculation on cast iron was also discussed． Key words~chill；cementite；undercooling；crystallizing nucleus 铸铁件生产中出现的白口就是游离渗碳体，由于 前者指物质的物态变化，后者表示物质以结晶的形式 硬度高，性脆，造成切削加工困难，轻则加快刀具的 出现，它既可以发生在物态转变时，也可以发生于不 磨损，重则造成断毁，中断生产。所以如何解决白口 变的同一物态下，而且，结晶必须有晶核的存在。当 问题一直是铸造工作者面临的课题。 金属 (合金)冷却降温至理论 (极其缓慢的冷速下) 液固相转变温度时，本应该结晶凝固，但由于此时晶 1 铸铁的结晶凝固过程 核数不足，晶核的产生是随着温度的下降与时间的推 1．1 铁液降温过程中成分的调整 移而逐步加速直至峰值开始结晶，因此不能结晶凝固。 凡由两种元素以上组成的液态合金，在降温过程 这时，液态金属被迫继续降温直至所生晶核足够时才 中必然 “调整”其成分以组成熔点最低的共晶体