固体材料的塑性变形.docVIP

第七章 固体材料的塑性变形 Chapter 7 Plastic Deformation 作业1：Identify the dislocation, in terms of its Burgers vector (Using vector notation) that can cross slip between the (111) and plane of an fcc crystal. Solution: 作业2：There are three slip systems on an fcc octahedral plane. Assume a 2 MPa tensile stress is applied along the [100] direction of a gold crystal, whose critical resolred shear stress is 0.91MPa. Demonstrate quantitatively that measurable slip will not occur on any of the three slip systems in the (111) plane as a result of this applied stress. Solution: The three slip systems in the (111) plane are (111) , (111) , (111) . Because [100], that is λ=, so ( resolred shear stress in (111)) is 0. Another two So：Measurable slip will not occur on any of the three slip systems in the (111) plane. 作业3.：An FCC crystal yields under a normal stress of 2 MPa applied in the [23] direction. The slip plane is (111) and the slip direction is [01]. Determine τcr for this crystal. (10 points) Solution: To solve this problem, we must find both cosθ and cosφ. This can be done suing the vector dot product: Cosθ= Cosφ= Solving equation for τcR and substituting the data given in the problem statement yields: τcR=(2Mpa)×(0.617)×(0.756)=0.933Mpa 作业4：假定某面心立方晶体可以开动的滑移系为[011]。试回答： （1）给出引起滑移的单位位错得相反矢量，并说明之。 （2）如果滑移是由纯刃位错引起的，试指出位错线的方向。 （3）指出上述情况下，滑移时位错线的运动方向。 （4）假定在该滑移系上作用一大小为：的切应力，试计算单位刃型位错线的受力的大小和方向。 （设晶格常数为a=0.2nm） 解：（1）为滑移方向上的一个原子间距（大小）。方向为滑移方向，故 （2）位错线一定在滑移面上，（与法线相垂直），且垂直于，则位错线方向与垂直。 （3）滑移时位错线运动方向即为方向 （4） 单位刃型位错受力大小，方向 方向位错线 方向∥。 作业5：若铜单晶可以在所有滑移系滑移，并且其表面平行于（001）， 试画出表面出现的滑移线痕迹，并确定滑移线之间的夹角。若铜单晶的表面平行于（111）， 情况又如何？ 解答： 表面平行于（001）面 滑移线痕迹，夹角90° 表面平行于（111）面 夹角60° 作业6：铜单晶拉伸时，若力轴为[001],临界分切应力值,问多大的拉伸应力能使晶体开始滑动？ 解：fcc，四个滑移面与(001)夹角相同， 即 每四个滑移面上的三条边中有一条与力轴垂直，分切应力为0，而另外两条边共计8条边等级。（即8个等级滑移系），其与力轴夹角为45°，即，则使晶体开始滑移的条件是， 故 作业7： 拉伸铜单晶体时，若拉伸力轴的方向为[001],。求（111）面上柏氏矢量的螺型位错线上所受的力（?）。 解：设外加拉应力