基干AHP方法作训服面料性能探析.docVIP

基于AHP方法的作训服面料性能分析 　　摘要：本文选择 5 种机织面料和 4 种针织面料作为作训服面料，分别对其物理性能、热湿性能进行测试，并通过层次分析法（简称“AHP”）将所测得的数据进行综合分析，计算出每种面料所占的权重。通过基于层次分析法的作训服面料性能分析，得出机织面料2#和针织面料4#较适合作训服面料，可采用在作训服适当部位拼接针织面料的方法来提高作训服的整体性能 关键词：机织面料；针织面料；性能；AHP 中图分类号：TS941.1 文献标志码：A An Analysis on the Performance of Combat Uniform Fabric Based on the AHP Method Abstract： In this article， five kinds of woven fabrics and four kinds of knitted fabrics were selected for being used as combat uniform fabric， and then the physical performance and thermal performance of these fabrics were tested respectively. Meanwhile a comprehensive analysis was carried out for the data obtained based on the analytic hierarchy process （AHP） method and the proportion of each fabric was calculated. The result shows that the woven fabric of 2# and knitted fabric of 4# are more suitable for combat uniform. In the end， the overall performance would be improved by the method patching knitted fabric in appropriate part of combat uniform. Key words： woven fabric； knitted fabric； performance； AHP 作训服是指军人在执行作战、训练、执勤等任务时穿着的军用制式服装，现代战争的特点对作训服的要求越来越高。作训服面料不仅要满足最基本的着装舒适性，还要保证不能影响士兵作战。因此对其综合性能进行客观准确的评价，是对作训服进行最优化设计的理论基础。本文是在目前07式作训服机织面料的基础上，通过选取良好性能的机织和针织面料，对机织面料和针织面料的性能进行测试和分析，运用层次分析法（analytic hierarchy process，简称“AHP”）的原理，构建织物综合性能评价的数学模型，客观量化织物的各种性能，以此提高作训服的整体性能 1 实验部分 1.1 实验材料 本课题选取 5 种不同的机织面料和 4 种不同的针织面料进行测试，面料基本参数如表 1 和表 2 所示 1.2 面料性能测试 面料性能测试之前按照GB/T 6529 ― 2008《纺织品 调湿和试验用标准大气》标准规定，将试样在温度（20±2）℃，相对湿度65%±4%的大气压环境中达到平衡 1.2.1 物理性能测试 （1）弯曲性 按照标准GB/T 18318.1 ― 2009《纺织品 弯曲性能的测定 第 1 部分：斜面法》，本实验采用LLY-01型电子硬挺度仪来测定面料的弯曲性能 （2）拉伸性 按照GB/T 3923.1 ― 1997《纺织品 织物拉伸性能 第1 部分：断裂强力和断裂伸长率的测定 条样法》，本实验采用YG065C电子织物强力机来测试面料的拉伸性，分别测试经纬向的断裂强力 （3）撕破性 按照GB/T 3917.2 ― 2009/ISO 13937-2：2000《纺织品 织物撕破性能 第 2 部分：裤型试样（单缝）撕破强力的测定》，本实验采用YG065C电子织物强力机来测试机织面料的撕破性，分别测试经纬向的撕破强力 （4）顶破性 按照GB/T 19976 ― 2005《纺织品 顶破强力的测定钢球法》，本实验采用YG065C电子织物强力机来测试针织面料的顶破强力 1.2.2 热湿性能测试 （1）透气性 按照GB/T 5453 ― 1997《纺织品 织物透气性的测定》，采用YG461Z型全自动透气性能测试仪测定面料的透气性