Researchonflowstresso_省略_ompressiondefor.pdfVIP

RARE METALS Vol. 25, No. 6, Dec 2006, p. 665 Research on flow stress of spray formed 70Si30Al alloy under hot com- pression deformation WEI Yanguang, XIONG Baiqing , ZHANG Yong’an, LIU Hongwei, ZHU Baohong, and WANG feng State Key Laboratory for Fabrication Processing of Non-ferrous Metals, Beijing General Research Institute for Non-ferrous Metals, Beijing 100088, China (Received 2005-08-23) Abstract: The flow stress of spray formed 70Si30Al alloy was studied by hot compression on a Gleeble-1500 test machine. The experimental results indicated that the flow stress depends on the strain rate and the deformation temperature. The flow stress increases with an increase in strain rate at a given deformation temperature. The flow stress decreases with the defor- mation temperature increasing at a given strain rate. The relational expression among the flow stress, the strain rate, and the deformation temperature satisfies the Arrhenius equation. The deformation activation energy of 70Si30Al alloy during hot deformation is 866.27 kJ/mol from the Arrhenius equation. Key word: 70Si30Al alloy; spray forming; flow stress; hot compression; Arrhenius equation [This work was financially supported by the National Basic Research Program of China (No. .] 1. Introduction experiment were cut and machined from a spray formed 70Si30Al preform to the size of 12 mm in New spray formed 70Si30Al alloy developed for diameter and 15 mm in length. Specimens were electronic packaging application has excellent heated at a rate of 10 K/s and then held at a test tem- physical characteristics [1-5], which include low perature of 923 K, 953 K, 993 K or 1033 K for 3 coefficiency of thermal expansion (6.8 × 10−6/K), min, and s