PPA通用资料（国外英文资料）.doc

PPA通用资料（国外英文资料） Para-polyphthalamide, a Polyphthalamide PPA under high temperature and high humidity condition, the tensile strength is higher than nylon 6 20%, higher than that of nylon 66. 20% higher than that of nylon, bending modulus greater hardness, resistant to long tensile creep. The ability of resistance to gasoline, oil and coolant is better than PA. This kind of high temperature resistant nylon material, can be a continuation of 200 ℃ high temperature resistant, and can keep good dimensional stability. Poly phthalic amide (hereinafter referred to as PPA resin with terephthalic acid or phthalic acid as the raw material of semi aromatic polyamide. Both half and amorphous, also has an amorphous state, the glass transition temperature at about 255 ° F. An amorphous state of PPA blocking performance is mainly used for places, half and amorphous PPA resin is mainly used in the injection molding processing, also used in other melting process. PPA PPA resin is stronger than fatty polyamide such as nylon 6 nylon 66. Its less sensitive to moisture; Better thermal performance; 而且蠕变、疲劳和耐化学品性能也好得多.如:含45％玻璃短纤维的PPA 树脂,抗张强度约276MPa,弯曲模量超过13786MPa,热变形温度(HDT549°F.即使矿物填料级的PPA ,抗张强度也能达到117MPa.PPA 树脂的延展性不如尼龙6尼龙66,然而,已经开发出未增强的冲击改性级PPA 树脂,其缺口悬臂梁式冲击强度高达20英尺·磅／英寸.所有的聚酚胺都吸收一定的水分,引起增塑作用和尺寸改变.例如尼龙6尼龙6,23°F下,相对湿度为100％时,能吸收8．9％的水分,这使其玻璃化温度由6．5°C降到一20℃,尺寸增加2．3％.相同条件下,PPA 树脂能吸收约6%水分,但其玻璃化温度Tg不会低于40℃,随同的尺寸增长不超过1．0％.正如前面所提过的,用玻璃增强的PPA 树脂有很高的HDT值,能耐受很高温度的短期作用,例如:一个供炉中或者在蒸汽相和在红外逆流团结过程中,PPA 树脂的热氧化稳定性使它能耐临时高温作用,玻璃增强级PPA ,20000小时内,其连续使用温度可达330°F.正常环境下,PPA 树脂通常对脂肪烃、芳香烃、氯代烃、酯、酮、醇和大多数水溶液表示出优秀的抗溶性.这类树脂不能经受极强的酸和强氧化剂的作用.可溶于酚和甲酚. 2. PPA is not inherently flame retardant, according to UL94 standard, flame retardant grade brand of grading of the resin for the VO, until 0.031 inch thickness. While other melting process can also be used, the vast majority of PPA resin is processed by radical injection molding process. Mix all the ingredients for the PPA predrying to less than 0.1% of humidity level, and t