天然透光石工艺(国外英语资料).docVIP

人造透光石工艺(国外英语资料) Now most manufacturers use Henan aluminum resin, usually with 885 resin The key technology of jade artificial stone is to add a certain amount of pattern agent to the artificial stone mixture, and the white pattern naturally comes into being Resin 100 aluminum hydroxide 220 copies to 240 copies (coarse powder of 100 mesh material accounted for 68% as well) 325 mesh fine powder as curing agent and accelerator at high temperature temperature a little low temperature add more general paste dosage in 0. Between 1% and 1% Process: on a glass plate coated with wax after mixing the mixture in the glass on the board in the expected 10 minutes 20 minutes after the gel curing, curing only reached 70% of the strength in 50 degrees to 60 degrees dry 2 hours to 4 hours can be, The equipment comprises a vacuum box vacuum mixer after the two key equipment and the purpose is to eliminate the bubbles in the mixture density better wrench Interested friends can get a wrench to try to do small ordinary glass can also get 1 or 2 meters of glass artificial stone correspondingly large, the only drawback is that there is a bubble Jade production process: 1, the proportion of the pattern material resin and powder 1:1 with good texture and color paste curing agent and accelerator are you going to do what color and what color paste, and then evenly spread pattern material in the mould (glass plate) and the material (100 to 220 copies of aluminum hydroxide resin 240 see temperature curing agent and accelerator dosage in 0 general paste. 1% to 1%) in uniform pattern material, finally into the vacuum box vacuum after 2 minutes to 3 minutes after the pattern of natural formation, but the grain line and net export is relatively small, if you want to be more beautiful jade texture that will put some additives: pattern agent, you can control the size of the pattern and line pattern thickness, As for the artificial stone in the stripes and wood grain is more simple, the main process