宝钢4号连铸机生产实践.pdfVIP

宝钢 4 号板坯连铸机的投产及生产实践 职建军 郁祖达 侯安贵 王洪兵 胡会军 宗震宇 （宝钢分公司炼钢厂） 摘要 为了满足公司品种、质量以及产能持续提升的发展需求，宝钢新增建了4 号板坯连铸机，该铸机由达涅利公司设计，采 用了结晶器电磁制动、轻压下等多项先进装备技术，于 2006 年 12 月投后，产能及品种拓展比较顺利，主要操作指标取得了持 续进步，品种质量满足了下工序要求，2007 年连铸坯产量达到了217 万吨。本文对操作指标和板坯质量进行了评价。 关键词 板坯 连铸 品种 质量 Startup and practice of No.4 slab CC at Baosteel ZHI Jianjun YU Zuda HOU Angui WANG Hongbing HU Huijun ZHONG ZhenYu steelmaking plant，Baosteel ABSTRACT In order to meet the developing requirement of output and quality of product of Baosteel, the No.4 slab continuous caster which is designed by Daniele Company of Italy was built, the machine run smoothly in aspect of producing and quality controlling after starting up in December,2006, the machine was equipped with such advanced apparatus and technology as EMBR and soft reduction, some operation index is improved continuely, slab quality meet request of downstream products, the output will reach 2.1 million ton in 2007.This paper describes the result of operation, slab quality is assessed. KEY WORDS slab continuous casting product quality 1 前言 4＃板坯连铸机是宝钢分公司“十一五”规划项目的重要组成部分，是炼钢厂二炼钢单 元挖潜改造的重大项目之一，该板坯连铸铸机是由意大利达涅利公司负责设计的两流高拉速 板坯连铸机，2006年 12月 16 日建成投产，成功浇铸了第一炉钢，建设周期仅 19.7个月， 比合同工期缩短了 146天，设计年产能力 280万吨，投产三个月实现品种覆盖，投产四个月 实现了月达标，2007 年产量达到 219 万吨。该连铸机生产的板坯厚度 230mm，宽度 900-1750mm，弧形半径 9.55m，冶金长度 41.46m，最高工作拉速 2.2m/min。与该连铸机相 匹配的前工序精炼装备主要有：5#RH,2#LF 炉，IR/UT,可以满足不同品种的生产工艺要求。 4 号连铸机主要为宝钢三热轧、五冷轧提供原料，产品涉及到从超低碳到高碳以及微合金钢。 二炼钢生产流程如图 1所示，阴影部分是为了满足品种和产能扩大需求而新增建的项目。 3#RH BF PTC ×2 250 BOF ×2 1450 SL ×2 IR-UT Hot PTC ×1