第七届中国国际钢铁大会 Development of Shipbuilding Steel Plate for High Heat Input Welding in Baosteel Jian Yang, Zhigang Ma, Kai Zhu, Ruizhi Wang, Qing Zheng Metallurgical Process Department, Research Institute, Baoshan Iron Steel Co., Ltd. Abstract: Oxide metallurgy technology, namely Excellent Heat Affected Zone Toughness Technology Improved by use of Strong Deoxidizers (ETISD Technology), has been developed by Baosteel. With delicate control of the vital elements in steel, deoxidation and continuous casting process, the desired micro-meter inclusions and the nano-meter precipitates in the steel plate can be effectively controlled. In the heat affected zone of the steel plate after high-heat input, the formation of coarse grain zone can be effectively inhibited, and the growth of intragranular ferrite can be greatly promoted. After two-electrode Vibratory ElectroGas Arc welding(VEGA) with the V-type groove and the high-heat input of 400 kJ/cm in single pass, excellent heat affected zone toughness can be obtained for the steel plates with the thickness up to 68 mm. Key words: high-heat input welding; heat affected zone; toughness; oxide metallurgy; inclusions. 1 Introduction In shipbuilding, architectural construction, offshore structure, multi-purpose gas carrier and linepipe fields, there are increasing demands of steel plates for high-heat input welding or with excellent weldability in recent years. With the development of large container ship, as for the sheer strake and hatch coaming of the upper deck to open to allow the loading and unloading cargo, the thicknesses up to 65 mm and yield strengths of 390 MPa are required for steel plates. In welding these thick plates, 1-pass Vertical Electro Gas Arc Welding(EGW), which is