摩擦材料原材料介绍.docVIP

无水氧化铝Aluminum Oxide (Anhydrous) Specific gravity 3.1 and more. Moh hardness 9. Look at the hardness. This is abrasive! Stable at high temperatures. If particle size is too big expect drum scoring. Fine powders (10 microns) will polish the drum or disc. Crystalline in structure it is similar to the mineral corundum. Aluminum oxide, like most abrasives nowadays, is manufactured rather than natural. Because of this improved control can be exercised over chemical composition and crystalline structure. Crystalline alumina has a conchoidal fracture, and the grains when crushed, or broken, possess sharp points and edges. （无水的氧化铝）比重大于3.1莫氏硬度9磨料，高的温度稳定性，如果微粒大划伤刹车鼓。10微米的细粉将抛光鼓轮或圆盘。结晶体在结构方面它与矿物刚玉相似。如同大多数磨料一样，现今，铝氧化物人造的好于天然的。因为这改进了化学的组成和结晶的结构的控制。当压碎时，结晶的矾土有一个蚌线的断口和颗粒，或断开的，拥有锐利的点和边。 氢氧化铝Aluminum Oxide (Hydrated) Aluminum Oxide Specific gravity 2.4 Moh hardness 3. More a filler than an abrasive. Tends to fade, but has good wear resistance. Will polish the opposing surface. 氢氧化铝比重2.4莫氏硬度3 .比磨料加得更多的填充物。有衰退趋势，但耐磨性好。将抛光对偶。 铝粉 96% pure aluminum in a granular form. Especially suited to low/medium duty applications. Blend of properties for good refinement and wear reduction of the material and rotor surface especially in lining/rail applications. 在一种粒状的形式方面的纯的铝96%。特别适用于中低负荷，混合料有好的特性和降低摩擦材料的磨损和对偶表面摩擦副的磨损 硅酸铝Aluminum Silicate Kyanite (Cyanite), an aluminum silicate, AlSiO often used in the calcined form will elevate friction levels. Kaolin or China Clay, AlSiO 2HO, are among the orthosilicates used in friction materials 蓝晶石（蓝晶石）、一个铝硅酸盐经常用于煅烧形式硅酸铝将升高摩擦水平。.高岭土或中国陶土，AlSiO 2HO，是其中正硅酸盐，用于摩擦材料。 煅烧氧化铝Fused Alumina (Alundum) alumina and is harder and more abrasive. (Typically 97% alpha alumina, 3% beta) It is less amorphous, has sharper fracture lines which impart more abrasive characteristics. Large particles will score the opposing surface. Quantities in excess of 1% (wt.) in a friction formula will wear the opposing surface and, in turn, the brake lining. 纯净矾土更多做磨料材料的熔化的矾土（刚铝玉）供给者。它是更少地非