国内常用钢材牌号替代各国钢材牌号.docVIP

German Chinese Material designation Mat. No. Former designat. Standard Remark Material designation Standard Title Remark Matching of properties: Engineering steels Engineering steels S185 1. 0035 St 33 DIN EN 10025 Q 195 GB 700-88 Unalloyed engineering steels accept only in killed condition Z, yield point and notch impact do not use energy not guaranteed S235JR 1. 0037 St 37-2 DIN EN 10025 KV at room temperature, Q 235 A GB 700-88 Unalloyed engineering steels F = unkilled, do not use do not use S235JRG1 1. 0036 U St 37-2 DIN EN 10025 KV at room temperature, Q 235 A GB 700-88 Unalloyed engineering steels F = unkilled, do not use similar unkilled S235JRG1C 1. 0121 UQ St 37-2 DIN EN 10025 KV at room temperature, unkilled, suitable for cold forming, S235JRG2 1. 0038 R St 37-2 DIN EN 10025 KV at room temperature, Q 235 B GB 700-88 Unalloyed engineering steels Z = killed similar unkilled not permitted S235JRG2C 1. 0122 RQ St 37-2 DIN EN 10025 KV at room temperature, Q 235 B GB 700-88 Unalloyed engineering steels Z = killed similar unkilled not permitted, suitable for cold forming, S235J0 1. 0114 St 37-3 U DIN EN 10025 KV at 0°C Q 235 C GB 700-88 Unalloyed engineering steels Z = killed or TZ = double-killed similar S235J0C 1. 0115 Q St 37-3U DIN EN 10025 KV at 0°C, suitable for cold Q 235 C GB 700-88 Unalloyed engineering steels Z = killed or TZ = double-killed similar forming, S235J2G3 1. 0116 St 37-3N DIN EN 10025 KV at -20°C, fully killed Q 235 D GB 700-88 Unalloyed engineering steels Z = killed or TZ = double-killed similar steel S235J2G4 1. 0117 DIN EN 10025 KV at -20°C, fully killed Q 235 D GB 700-88 Unalloyed engineering steels Z = killed or TZ = double-killed similar steel S235J2G3C 1. 0118 Q St 37-3N DI