多点成形中压痕的形成与控制方法-吉林大学学报.PDF

Vo l. 34 No.l 第 34 卷第1 期 吉林大学学报(工学版) 2004 年 1 月 Journal of Jilin University (Engineering and Technology Edition) Jan.2004 文章编号: 1671- 5497(2004)01- 0091 一 06 多点成形中压痕的形成与控制方法 刘纯国，蔡中义，李明哲 (吉林大学辍锻工艺研究所，吉林长春 130025) 摘 要;对多点成形中压痕缺陷的形成及影响因素进行了力学分析，指出弹性垫技术可以明显 地消除压痕缺陷。采用多点压机及多道多点成形技术改变了约束方式及变形路径，因而有效 地抑制了成形缺陷的产生，提高板材的成形极限并实现了大变形量成形。通过典型的数值模 拟及成形实验说明了弹性垫技术及多道成形技术消除压痕缺陷的有效性。 关键词:板材;多点成形;压痕 文献标识码:A 中图分类号:TG301 Dimple formation and its elimination in multi-point forming for sheet metal LIU Chun-guo , CAI Zhong-yi , LI Ming-zhe (Roll Forging Institute ,Jilin University , Changchun 130025 , China) Abstract:The formation of the defective dimple and its influencing factors in multi-point forming(MPF) process of sheet metal were analysed mechanically and it was indicated that dimpling defect could be eliminated evidently with elastic cushion. In the forming processes of MPF press and multi-step MPF ,the restraint condition and deformation path of sheet metal were changed , and the forming defects wer巳 subdued, then the forming limitation was improved and large deformation could be achieved. Numerical results and forming tests of typical specimens demonstrate that dimples are eliminated effectively by means of elastic cushion and multi-step MPF. Key words:sheet metal;multi-point forming;dimple 多点成形是金属板壳类件的一种柔性加工方法[1-3] 。这种方法以一系列规则排列的冲头(或称基 本体)点阵代替传统的整体模具，通过对各冲头运动的实时控制，自由地构造出冲头点阵的成形面，以成 形面代替传统模具成形出各种形状的三维板材曲面。采用多点成形技术不需另外配置模具，可以节省 大量的模具设计、制造及修模调试的费用。所加工的零件尺寸越大、批量越小，这些优越性越突出。 压痕[4] 与起皱缺陷是影响多点成形件质量的主要因素，因此对其进行深入、系统的研究，寻找抑制 缺陷产生的方法具有十分重要的意义。 收稿日期 :2002-1