攀枝花学院本科毕业设计（论文） 真空实型铸造用涂料性能测定方法研究 学生姓名： 陈 贵 学生学号： 200310519091 院（系）： 材 料 工 程 系 年级专业： 2003级材料科学与工程 指导教师： 周 洪 高级工程师 助理指导教师： 二〇〇七年六月 摘 要 真空实型铸造被本文以模拟生产实际条件设计检测方法为指导思想，提出了真空实型铸造用涂料的随着麻纤维加入量的增加，涂料透气性稳步提高，当涂料中含0.5%的麻纤维时，透气率稳定在140～160，比不含麻纤维的涂料提高了3倍；同时，涂料强度提高20%，麻纤维的加入对涂料的耐磨性影响不显著。  ABSTRACT The vacuum evapourative pattern casting is praised for the green cast of the 21th century, but, there usually are casting defects (blistering, sandbuckle, surface carburization, etc.) on the cast surface. The main reason is that the method of measurement to mold coating property is different from the factory practice, and the observed value is different from the actual nature. This paper simulated the factory practice to measure the mold coating property, for example permeability, strength, painting performance, and dripping performance. The result shows, the permeability and strength are improving along with the hemp fiber joining the mold coating. The permeability is up to 140-160, the strength raises 20% and the wearability remains initial value, when the numb fiber is 0.5% of the mold coating. Key words mold coating, permeability, strength, test methods 目 录 摘要…………………..……………………………………………………………………………Ⅰ ABSTRACT………………………………………………………………………………………Ⅱ 1 绪论………………………………………………………………………………………………1 1.1 选题理由…………..…………………………………………………….…………………1 1.2 项目研究目的………………………………………………………………...……………2 1.3 项目研究意义…………………………………………………………………...…………2 2 真空实型铸造用涂料性能测试研究现状………………………...………………………3 2.1透气性的测试………………………………………………………………………………3 2.1.1 常温透气性的测试……………………………………………………………………3 2.1.2高温透气性的测试………………..……………………………………………………4 2.2 强度的测试…………………………………………………………………...……………5 2.3 涂挂性、滴淌性的测试……………………………………………...……………………6 3 涂料性能测试方法设计………………………...……………………………………………8 3.1 高温透气性测试方法设计………………………………………………………………8 3.1.1 测试用装置…………………………….………………………………………………8 3.1.2 测试方法………………………………………………………………………………8 3.2 强度测试方法设计…………………………………………………………………………10 3.2.1 测试用装