电渣压力焊连接（Electroslag welding connection）.docVIP

电渣压力焊连接（Electroslag welding connection） In multi-storey and high-rise buildings, connecting the vertical steel frame column or shear wall by electroslag pressure welding connection, simple construction, convenient operation, low cost. However, the construction by the operation method, effect of voltage and current and other factors, often cause the quality defects of welding joints, such as axis, joint welding bag is folded, thin and large joint, the bad welding package unevenness, porosity slag, not drip phenomenon. The steel welding specification, welding package should be uniform, the prominent part of at least higher steel surface 4mm electrode and reinforced contact, no obvious burn defect, framed bent angle joints is less than 40; the joint axis deviation does not exceed 0.d (d bar diameter), and more than 2mm. In order to avoid these defects, we take corresponding preventive measures, good effect. The specific measures are as follows. Offset on axis Causes; welded steel end distortion phenomenon or fixture is not installed correctly without clamped steel; fixture extrusion pressure is too large, resulting in reinforced dislocation. Before welding has good shaking clamping bar, the upper and the lower clamp itself has reinforced dislocation, deformation or distortion. Preventive measures; before welding inspection of steel bar end, not straight part should be removed or corrected, mounting fixture must be correct, held under the steel concentric, upper and lower clamp can clamp clamping uniform reinforcement; reinforced after shaking is prohibited under the steel bar, in order to avoid dislocation or fixture deformation, distortion, check if the clamp and clamp fastening deformation before the operation, the fixture can not be used, the clamp should be replaced or repaired. Joint bending The causes of welding fixture; remove prematurely, joints of molten metal is not completely cured, the joint strength and stiffness is very small, can not support the upper pa