A335P92 焊缝局部热处理施工工艺改进的研究与分析 姚鹏乐 宋国营 张丰收 李俊峰 黄振华 河南华电金源管道有限公司 河南郑州 450051 摘要：为解决生产过程中 A335P92 局部热处理时出现的硬度异常等问题，经多方面的学习及对比试验，对局部热处理工艺 操作进行了研究与分析，确定了一种适用于现场及工厂的局部热处理施工工艺。通过试验发现：热处理自动控温柜数字表可 能会出现误差；找到最简单易行且不影响结果的包口方式；在实际处理过程中，取规程中参数中间或下限值可能会出现硬度 偏高的情况，取上限能满足要求。 关键词：局部热处理；硬度；工艺改进 Abstract ：In order to solve the problems of A335P92 steel in local heat treatment,this paper studied and analyzed the process improvements of local heat treatment with widely learning and comparative experiments,and determined a local heat treatment technology which is suitable for the practical production.Through our experiments ，it is found that there may be errors in the digital multimeter of heat treatment Automatic Temperature Control Cabinet.And we found the most simple operation pro cess that doesnt affect the results.In the practical production,the hardness of workpiece may be higher than normal if the heat treatment temperature is the intermediate ratio of specification.However, the hardness is able to meet the requirement of quality inspection and application if the heat treatment temperature is the upper limit ratio. Key words ：Local heat treatment; Hardness; Process improvement 0 前言 的不足，经多方面的实验及讨论，得出一整套适 用于局部热处理的方法及工艺。 进入20 世纪70 年代以来，由于大容量、高 参数的火电机组相继安装，焊接热处理工作量大 1 实验准备、材料和设备 幅度增加，随着使用的钢管品种多样化，对焊接 1.1 实验准备 热处理过程的要求越来越高，特别对于 A335P92 本次试验的对象是某电厂再热热段管道，规 来说，热处理过程尤为重要。近年来，关于A335P92 格为ID387x25，材质A335P92，结构形式为直管+ 局部热处理的论文及成果有很多，但多偏重于理 弯头。 论或微观方面的分析，涉及到具体操作时，众说 该管道的焊接方式为 GTAW+SMAW+SAW，焊缝打底 纷纭。对本公司来说，A335P92 焊缝经局部热处 采用Thermanit MTS 616，OD2.4 的氩弧焊丝，手 理后，焊缝硬度值偏高，甚至超出标准要求，造