人防地下室工程裂缝处理方案（Crack treatment project of basement）.docVIP

人防地下室工程裂缝处理方案（Crack treatment project of basement） Repair plan of reinforced concrete wall and cracks in civil air basement of Longhu Bay Our construction of the Longhu Bay (VV L7 project) basement project, the main project has been completed the construction of the basement, the basement surrounding backfill has been completed in most; in the basement in quality inspection, found that the exterior wall of the underground small sealing screw at the wet seal, the sealing screw in individual water leakage in roots; the basement roof with a layer of negative in 2013 after pouring the emergence of several shall not crack, appear in the rain water seepage joints, causes and treatment methods for my company project Department of cracks for meeting analysis. First, the cause of the formation of cracks 1, wall sealing screw mainly due to water seepage, demolition early after concrete pouring template, removed when the concrete strength is too low, the water screw holding force is small, because the formwork Chaimo of screw vibration, beating, making part of the screw loosening in concrete, it eventually leads to water penetration. The main reason for cracks in the roof, basement 2: 1, concrete water cement ratio is too large, the shrinkage of concrete, concrete cover; the plastic film covered with other materials are not consolidated, borne by the wind, the soldiers failed to timely watering maintenance; complete the construction, the concrete pouring, the upper stacking time early, the impact force on the surface of the crane transporting materials from falling; cracking time, this part belongs to the early formation of crack crack, through nearly a month of continuous observation, roof cracks are basically stable, not to continue to expand the trend. Two, crack treatment 1, the strength of concrete meets the design requirements, in order to ensure the durability of the use of housing, prevent the roof reinforcement corrosion, cracks closed treatment. The sealing material