铁素体可锻铸铁的生产工艺研究 摘要：铁素体可锻铸铁断口外缘为脱碳的表皮层，心部组织为铁素体+团絮状石墨的可锻铸铁。珠光体 The research of Ferritic Malleable Cast Iron Abstract: Ferritic Malleable Cast Iron fracture edge for decarbonization of the epidermal layer, heart tissue for ferrite and graphite clusters of malleable cast iron. Ferritic Malleable Cast Iron Microstructure of ferrite matrix graphite clusters. Because of the annealing process of furnace gas oxidation, often make the casting surface has a decarburized layer, and the center part of the microstructure is different. Through heat treatment of pearlite to austenite transforms into, namely the austenitizing, and then austenite continuously into the austenite and disappear gradually, graphite clusters corresponding to generate, cooling, carbon in austenite reduced solubility and precipitation of supersaturated carbon, deposited on the graphite, organized into pearlite and graphite clusters, continue to cooling, pearlite decomposition, forming the white part of the iron in the body, the black part of the map of flocculent graphite. Keywords: Ferrite; heat treatment; cast iron; casting microstructure 目 录 第一章 绪论 1 1.1 可锻铸铁概况 1 1.2 铁素体可锻铸铁的组织 1 1.2.1铁素体可锻铸铁的组织特点 1 1.2.2铁素体可锻铸铁的性能 1 1.2.2.1 力学性能及影响因素 1 1.2.2.2 铸造性能 2 1.3 研究内容及目的 2 第二章 实验方法 3 2.1 化学成分的选定原则 3 2.2铁素体可锻铸铁配比计算 3 2.3热处理工艺的选定 4 2.4 实验用原材料、仪器设备及实验步骤的制定 6 2.4.1本次实验所用原材料 6 2.4.2本次实验所用仪器设备 6 2.4.3实验步骤 7 2.4.3.1制作砂型 7 2.4.3.2熔炼 7 2.4.3.3浇注 7 2.4.3.4热处理 7 2.4.3.5金相制作与观察 7 第三章 结果分析 8 3.1 实验所得金相组织 8 3.2 实验所得金相组织分析 8 第四章 结论 9 参考文献 10 第一章 绪论 1.1 可锻铸铁概况 可锻铸铁是将白口铸铁通过固态石墨化热处理（包括有或无脱碳过程）得到的具有团絮状石墨的铁碳合金。采用不同的热处理方法，可以得到具有不同组织和性能的可锻铸铁，即黑心可锻铸铁、珠光体可锻铸铁和白心可锻铸铁。 　　当将白口铸铁毛坯件在密封的退火炉中进行热处理，即在中性炉气条件下退火时，得到的铸铁组织中有呈团絮状的石墨（退火碳）存在。这种石墨虽不很圆整和紧密，但它对基体的割裂作用则比灰铸铁中的片状石墨要小得多，因此它能使铸铁得到较高的强度及良好的韧性。铸铁的基体可以通过热处理来加以控制。使之成为铁素体或珠光体。用这种方法得到的铁素体基体可锻铸铁因组织中有石墨存在，因而铸铁的断面呈暗灰色，而在表层经常有薄的脱碳层呈浅灰色，故通称为黑心可锻铸铁。而珠光体可锻铸铁则是以其基体命名的。 1.2 铁素体可锻铸铁的组织 1.2.1铁素体可锻铸铁的组织特点 铁素体可锻铸铁的金相组织为铁素体基体加团絮状石墨。由于退火过程中炉气的氧化作用，常使铸件表面有一脱碳层，与中心部位的显微组织有所不同。 可锻铸铁中心部