EPS 颗粒轻质混合料在路堤施工中应用.docVIP

EPS 颗粒轻质混合料在路堤施工中应用摘要： EPS 颗粒混合轻质混合料代替普通路堤填料，有效利用了废弃沉井排砂土，同时对保护环境具有一定意义。本文以泰州大桥接线工程F01标匝道EPS 颗粒混合轻质路堤填筑为实例，通过室内试验确定EPS颗粒、沉井排砂土与水泥配比，并经击实试验确定现场EPS 颗粒混合轻质路堤压实度检测标准。针对压实度与碾压组合、碾压遍数、无侧限抗压强度、弯沉及养护龄期等相关关系进行分析。 关键词：EPS颗粒，沉井排砂土，路堤施工 Abstract: the EPS particle mixing light mixture instead of common embankment packing, effective use of the abandoned in open caisson row sandy soil, at the same time, which is significant for protecting the environment. In this paper the connecting engineering F01 standard taizhou bridge ramp EPS particle mixing light filling the road embankment as an example, through the laboratory test sure EPS particles, open caisson row with cement sand ratio, and the compaction test to determine the EPS particle mixing light embankment compaction degree testing standards. For the compaction and rolling combination, compaction quantities, no lateral restraint compressive strength and deflection and curing age related analysis. Keywords: EPS grain, open caisson row of sand, embankment construction 中图分类号： TU528.062 文献标识码：A文章编号： 一、概述 泰州大桥接线高速公路穿越长江滩涂地带，建设土源尤为紧缺，而沿线沉积了大量江砂，且南锚锭有6多万方沉井排砂土的弃方，如果能够通过与EPS颗粒沉井排砂土与及水泥混合形成路堤的填筑材料，可节省大量的土地资源与工程投资。同时将EPS颗粒回收料变废为宝，具有较好的应用前景和很好的经济、社会和环境效益。本次EPS颗粒混合轻质路基施工段落全部分布在F01扬中互通区的匝道上。 二、 试验准备 EPS是发泡聚苯乙烯（Expanded Polystyrene）的英文缩写，EPS颗粒混合轻质土的主要成分包括原料土、固化剂（水泥）、EPS颗粒和水，经搅拌凝固后而成的一种混合轻质材料，它的低密度决定了轻质土路堤自重造成的路基沉降要远小于普通灰土填筑路堤，这使得与工程安全性相关的材料强度尤为重要。对EPS颗粒混合轻质土强度的研究致力于探索其强度与原材料添加量、龄期、施工技术之间的关系。依据高速公路轻质路堤填筑的需要，主要进行EPS颗粒混合轻质土中沉井排砂土颗粒分析试验、自然堆积密度试验；EPS颗粒安全性检测（阻燃型）、物理性能检测；水泥常规性能检测及混合料击实试验、无侧限抗压强度、弯沉检测等。 1 .试验材料参数 土：采用泰州大桥南锚沉井排砂土作为原料土进行填筑，自然堆积密度为1281kg/m3， EPS颗粒：阻燃型，不可降解，颗粒大小均匀，密度控制在11-15kg/m3。原料产地是江苏嘉盛化学品工业有限公司，物理性质及化学成分列于表1中。 表1 EPS颗粒原料物理性质及化学成分 表2水泥物理性能及力学性能 2.击实试验 从EPS 颗粒混合轻质材料的击实结果来看，轻、重型击实方法相差较小，但可以看出，随着水泥含量增加，最大干密度逐渐增大，最佳含水量逐渐增大。通过大量试验确定EPS：土=4：6（自然堆积体积比例）及水泥掺量为土的质量的10%，最大干密度及最优含水量分别为1.202g/cm3和15.2%。 3. 强度试验 在施工应用前，在沉井排砂土中掺加不同含量水泥，并击实制成高100mm、直径10mm的圆柱型试样，密封放置潮湿环境下养护。EPS：土=4：6（自然堆积