探析建筑施工现浇钢筋砼楼板裂缝.docVIP

探析建筑施工现浇钢筋砼楼板裂缝摘 要：钢筋混凝土梁板规范允许带着裂缝工作,混凝土内部存在诸多微裂缝，这是很多人都明白的,建筑商和施工商也在大力的鼓吹这些裂缝不影响房屋的使用功能，不会造成房屋的质量问题。但这不等于说楼板可任意开裂,实际施工应严格控制开裂,以免影响结构的耐久性。 关键词：建筑施工；现浇钢筋；砼楼板；裂缝 Abstract: reinforced concrete beam plate specification allows with working cracks, concrete interior is put in a lot of micro cracks, this is a lot of people do not understand, builders and construction also vigorously advocated these cracks do not affect the use of housing functions, will not cause the housing quality problems. But this does not mean that the floor can be arbitrary crack, the actual construction should be strictly controlled to crack, so as not to affect the durability of the structure. Key words: construction; cast-in-place reinforced concrete floor slab; crack; 中图分类号：TU71文献标识码：A 文章编号： 1. 现浇钢筋砼楼板产生裂缝的原因 1.1 设计方面。 目前的砖混结构住宅普遍存在房间面积过大，有的单块板尺寸达4.5m×5.4m，板厚达12~15cm，客厅与餐厅相连近40m 2；有的阳台外挑达2.1m，有纵向墙体开设过大窗洞。这些过大的房间、阳台、门窗洞口使得砖混结构墙体这个主要承重构件布置不足或严重削弱。现浇楼板边端约束，受此影响发生改变，有的地方约束强，有的地方约束弱，使楼板整体变形不一致。冷轧带肋钢筋在钢筋砼现浇板中的使用，在满足楼板及板最小配筋率的情况下节约了大量钢材，但与普通钢筋相比却降低了板的配筋含量，同时冷轧带肋钢筋较常规筋细，特别是板负弯矩筋，在施工中易受弯变形和移位。 单块板面积过大的现浇钢筋砼板变形较大，受温度、干缩、板端约束以及施工等影响较敏感。其板边端约束以及温度收缩影响而产生角拉应力引起斜向裂缝产生较严重，当角拉应力很大时，将导致裂缝产生并贯通板厚。对此，设计人员依然按照常规方法对大跨及面积较大、较厚板进行设计，而对其变形及抗裂未予重视，仅通过引用国家标准或标准图集的构造措施，更很少单独提出有关防裂的要求和措施，更没有对这些措施的可行性进行调查和总结。 现阶段的砖混结构设计，考虑房屋整体强度的抗震设计措施较多，对钢筋砼现浇模板与承重砖墙体这两种不同材料温度应变的变形协调问题未予考虑，控制温度变形的措施较少，加剧了现浇板裂缝的产生。 1.2 施工方面： 随着新工艺、新材料、新设备的使用，工程建设的工期得以缩短，三五天建一层楼房的例子屡见不鲜，商品砼的使用，加快了砼的浇灌速度，但带来的问题却是水灰比过大，浇筑中水分蒸发过快，砼成型容易开裂；粗骨料较常规小且棱角小；输送泵输送出的砼不均匀，离析现象严重，砼拌合物的粘聚力变差，对砼的强度与耐久性产生一定的影响。另外，施工措施不当，输送泵输出的砼直接作用于绑扎好的板钢筋上，容易使板负弯矩筋弯曲变形与移位，造成砼成型后产生较大的收缩和开裂，而钢筋弯曲变形、移位，会使钢筋保护层过大，相应减小了现浇楼板砼的有交截面高度，使砼楼板出现裂缝。 人们在把主要精力用于如何加快施工速度以提高经济效益的同时，很少在砼构件的养护措施方面下工夫。施工现场的砼大多数采用直接浇水养护，很少采有覆盖草席浇水养护，其结果使砼早期失水严重，在强度生成期不能时时处于湿润环境，即砼凝固因早期失水过快而导致开裂，砼硬化后因干缩和温度过大而引起的收缩裂缝，这些裂缝往往出现在板中部附近，且裂缝不规则数量较大。 现浇钢筋砼楼板过早地承受施工荷载的作用，对其强度生成损害较大。现在的施工现场往往是楼板砼刚浇筑完，第二天即开始放线，第三天即在其上堆放砖、砂浆，搭设砌筑脚手架并砌筑上一层的砖墙体，这对于刚处于硬化期和强度增长期的砼极易因外力的作用和震动而产生下沉和变形，在砼楼板表面产生裂缝。另外，模板刚度不足或支