扩散部分课件.ppt

Chapter 8. Diffusion 扩散 8.1 Introduction 物质迁移的两种方式： Convection, diffusion For gas and liquid: Convection and diffusion For solid: Diffusion diffusion of Cu-Ni couple: 8.1.1 Diffusion Mechanism Vacancy Diffusion/Mechanism 空位扩散/机制 8.1.1 Diffusion Mechanism Interstitial Diffusion/Mechanism 间隙扩散/机制 8.1.1 Diffusion Mechanism Interstitial Diffusion/Mechanism 间隙扩散/机制 8.1.1 Diffusion Mechanism Transposition Diffusion/Mechanism 换位扩散/机制 8.1.2Requirement of Solid state固态扩散的条件 （1）Temperature high enough 温度足够高； （2）Long enough 时间足够长； （3）Can form Solid Solution 扩散原子能固溶； （4）Driving force 具有驱动力。 8.1.3 Categories of Diffusion Diffusion: Mass transport by atomic motion. Interdiffusion (or impurity diffusion): Diffusion of atoms of one metal into another metal. Self-diffusion: Atomic migration in pure metal. 8.1.3 Categories of Diffusion Diffusion direction: Downhill diffusion and Uphill diffusion: Form a new phase or not: Atomic diffusion and Reaction-diffusion 8.1.4 应 用 扩散在材料的生产和使用中的物理过程有密切关系。 For example：Solidification凝固、Segregation偏析、 Homogenizing Annealing均匀化退火、 Recovery and Recrystallization after cold-worked 冷变形后的回复和再结晶、 Solid phase transformation固态相变、 Chemical heat treatment化学热处理、 Sintering烧结、Oxidation氧化、Creep蠕变等等。 8.2 Diffusion Law diffusion flux ( J ) 8.2 Diffusion Law 8.2.1 Fick’s First Law (1855) 菲克第一定律 8.2.1 Fick’s First Law (1855) 菲克第一定律 8.2.2 Fick’s Second Law 菲克第二定律 Nonsteady state diffusion 非稳态扩散 8.2.3 Applications 扩散方程的应用 A Solution of Fick’s second law for a semi-infinite solid 8.1.3 Applications 扩散方程的应用 例一：将纯铁放于渗碳炉内渗碳，假定渗碳温度为920℃，渗碳介质碳浓度Cs=1.2%，D=1.5×10-11m2/s，t =10h。 求表层碳浓度分布； 如规定浓度渗层深度为表面至0.3%C处的深度，求渗层深度。 例二：有一20钢齿轮气体渗碳，炉温为927℃，炉气氛使工件表面含碳量维持在0.9％C,这时碳在铁中的扩散系数为D＝1.28x10-11m2/s,试计算为使距表面0.5mm处含碳量达到0.4%C所需要的时间? 例三：上例中处理条件不变，把碳含量达到0.4％C处到表面的距离作为渗层深度，推出渗层深度与处理时间之间的关系，层深达到1.0mm则需多少时间? 8.3 Factors that Influence Diffusion Diffusion Coefficient 扩散系数公式 8.3 Factors that In