1074转炉双渣法少渣炼钢工艺新进展.pdfVIP

2016 年（第十九届）全国炼钢学术会议论文集 转炉双渣法少渣炼钢工艺新进展 丁瑞锋 冯士超 王艳红 （鞍钢股份有限公司技术中心，鞍山114009） 摘要：介绍了国内外典型双渣法少渣炼钢工艺的技术现状及新日铁、浦项、首钢、宝钢和武钢等厂家在排渣制度、枪位操作以及留渣操 作等工艺的优化措施。转炉双渣法利用转炉内自由空间大，反应动力学条件优越，生产成本较低，而且操作简单，无需新增设备，引起 了国内外、特别是受设备限制的钢厂的广泛关注。 关键词：转炉双渣法 炼钢工艺优化 NEW PROGRESS OF DOUBLE-SLAG STEELMAKING PROCESS FOR CONVERTER Ding Ruifeng Feng Shichao Wang Yanhong （Ansteel Technology Center, Anshan, 114009, China ） Abstract: The current technical situation of typical double-slag steelmaking process both at home and abroad for converter was described, as well as the optimization measures of slag discharge, lance control, slag-remaining and other aspects that adopted in Nippon steel, Posco, Shougang, Baosteel, Wusteel and so on. Because of the larger free room, superior conditions of reaction kinetics, lower production costs, together with the simple operation and no need of new equipment, the double-slag process for converter attracted steel plants extensive attention in the domestic and overseas, especially some plants that restricted by the equipment. Key words: Converter; Double-Slag Process; Steelmaking Process, Optimization 1 前言 目前，日本各大钢铁企业广泛采用转炉“双联法”操作工艺，将铁水脱磷预处理移到转炉内进行，利用转炉内自 由空间大，反应动力学条件好，解决了超低磷钢的生产难题，且生产成本较低。但由于受设备和产品的限制，也有 在同一座转炉上连续进行铁水脱磷和脱碳吹炼的操作模式，类似传统的双渣法，并且该工艺还可将脱碳渣残留在炉 内用于下一炉脱磷，被认为是目前渣量最少的转炉生产洁净钢工艺路线，而且该工艺操作简单，无需新增设备，已 在国内外特别是受设备限制钢厂的广泛采用。 2 典型的双渣法少渣炼钢工艺 早在2009 年，新日铁采用MURC （Multi-Refining Converter）双渣脱磷工艺比率已达53%，韩国浦项钢铁公司 和现代制铁公司唐津钢厂也采用了类似的工艺；国内应用比较成熟的是首钢“留渣+双渣”SGRS工艺，主要生产优质 中厚板､管线､桥梁、高层建筑以及海洋平台用钢板等超低磷钢种。新日铁大分厂MURC 工艺如图1 所示。 同一转炉 脱碳渣留渣 装入铁水和 脱磷吹炼 脱磷渣 脱碳吹炼 废钢 “一倒”排渣 出钢，炉渣留在炉内