利用宽城县铁尾矿制作免烧砖的研究.doc

利用宽城县铁尾矿制作免烧砖的研究 何绍顕 （天津理工大学 材料科学与工程学院，天津300191） 摘 要 本文针对宽城铁尾矿对矿区污染严重问题，提出使用宽城铁尾矿制造免烧砖的思想，在本文中对铁尾矿免烧砖的成型工艺进行了研究，确定了利用宽城铁尾矿制造免烧砖的最佳配比方案、养护条件和加压压力，所制备的免烧砖样品符合“非烧结垃圾尾矿砖JC/T422-2007”的MU15标准,比同等强度的免烧砖水泥用量降低一倍。本项目不但解决了铁尾矿的综合利用问题，还大大提高了免烧砖的质量，降低了成本。 关键词： 铁尾矿 高炉水淬渣 免烧砖 Study on preparation of non-burnt brick from iron tailings of kuancheng HE Shao-xian ,JIN Jing ,ZHENG Jian ,MU Qiao ,ZHOU Xiao-yu (School of Materials Science and Engineering , Tianjin University of Technology , Tianjin 300191 ,China) ABSTRACT The article is based on Iron tailings causing serious pollution problem in mining area in KuanCheng, proposing the thought of using Iron tailings to produce Baking-free brick. In the article the molding process of Baking-free brick of Iron tailings were studied. The best proportion schemes, the maintainance condition and compression pressure of Baking-free brick were determined. The sample of Baking-free brick prepdprepared was complied with the MU15 standards of “The nonsintering waste tailings brick JC/T422-2007” and lower the cement volume of Baking-free brick double than equal intensity. The project not only solves the comprehensive utilization problem of Iron tailings, but also improves the quality of Baking-free brick and reduces the cost. Key Words：Iron tailings Furnace water-quenching slag Baking-free brick 0．引言 近年来，宽城县矿业经济发展迅速，矿业生产成为全县的支柱产业，但在矿业蓬勃发展的同时，也产生了大量固体废弃物——铁尾矿和废矿渣。如果按照一吨铁精粉产生1.6吨铁尾矿来计算，本县在2006年生产550万吨精铁粉，产生的铁尾矿为867万吨。铁尾矿由于粒度细，造成扬尘和水质污染相当严重。堆放铁尾矿的铁尾矿库投资巨大，如果铁尾矿库的建造不达标，则存在巨大的环境污染和安全隐患。高炉水淬矿渣由于块大，密度小，堆放侵占农田，同样造成极大的危害。铁尾矿和高炉水淬矿渣含有大量的非金属矿物，在建材方面有很好的利用价值。 综合利用铁尾矿制作免烧砖立足于大量消耗尾矿、产品销路广、能耗低和生产工艺简单【1】~【3】。不仅能够保护环境，实现低碳排放，而且为社会和企业带来巨大经济效益。本课题通过对河北省宽城县铁尾矿成分、密度和粒度研究，并分析铁尾矿活性的激活剂，研制出以宽城铁尾矿及当地资源为原料，生产低成本、高质量免烧砖的配方和工艺，用免烧砖代替当地的使用的烧结砖可以为当地环境保护和经济发展带来巨大效益。 1．铁尾矿分析 1.1铁尾矿化学成分 经过测试，河北省宽城县地区铁尾矿属于高硅型铁尾矿，其中含有二氧化硅77%，三氧化二铝5.1%，不含铅、镉、铬、汞、砷等有害元素和放射性物质，是优质的建筑材料成分，其化学成分如表1。 表1 宽城铁尾矿化学成分 % 成分 SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O 含量 77 5.1 2.6 6.9 4.7 2.4 1.5 根