金属表面处理工艺（Metal surface treatment process）.docVIP

金属表面处理工艺（Metal surface treatment process） Surface blackening treatment process Surface blackening of steel parts processing, also known as barffing. Black treatment now commonly used methods have the traditional alkaline heating and blackening of the late appearance of two kinds of room temperature. But the blackening process at room temperature is not very good for low carbon steel. A3 steel is slightly better by alkaline blackening. Alkaline black fractionize comes out, have again black and two black distinction. The main components of the black liquor are sodium hydroxide and sodium nitrite. When youre black, you need a good tolerance of temperature. You can get a nice surface between 135 and 155 degrees Celsius, but it takes only a little time. In the actual operation, the need to pay attention to is the workpiece before blackening and rust removing oil quality, and blackening after passivation of immersion. Blackening quality is often due to these processes and change. Blue liquid metal Using alkaline oxidation or acid oxidation; to form a layer of oxide film on metal surface to prevent metal surface corrosion, this process is called blue. The black metal surface by the blue treatment after the formation of the oxide film, the outer layer is mainly magnetite, the inner layer is feo. A blue, alkaline oxidation liquid 1. formula: 50 ~ 100 grams of sodium hydroxide and sodium nitrate from 600 to 700 grams of sodium nitrate 100 ~ 200 grams 1000 grams of water 2. system method: according to the formula after measuring, in the mixing conditions, in turn each material to add, dissolve, mix evenly. 3. instructions: (1) the metal surface must be cleaned and dried before the basket can be processed. (2) metal devices blue to deal with the relevant condition and the metal carbon amount, and the solution temperature and the metal component can refer to the following table in the processing time. The carbon content of metals,% operating temperature (DEG C), and processing t