YY-503在无卤阻燃PPO-SEBS共混体系中的研究及应用(10-27投稿).docVIP

YY-503在无卤阻燃PPO/SEBS共混体系中的研究与应用 阳范文1,谭铭浩1，张良1，徐克谋2 （1.广州医科大学生物医学工程系，广东广州510182；2.广州源泰合成材料有限公司,广东广州，510635） 摘 要：系统研究了多功能助剂YY-503对无卤阻燃PPO/SEBS弹性体的拉伸性能、弯曲性能、流变性能、表面光泽度和阻燃性能的影响：随着YY-503用量增加，材料的拉伸强度、断裂伸长率呈现先增加然后减小的变化趋势，缺口冲击强度和表面光泽度依次增大。YY-503的用量0.5～1%时，材料的阻燃性能达到V-0级，表面光泽度比未添加时提高约20%，L值增比未添加时提高3以上。YY-503具有优异的耐热性能，可改善氢氧化镁与塑料基体之间的界面结合力，降低体系的摩擦力，避免体系剪切力过大引发共混物的降解和颜色黄变等问题。 关键词：无卤阻燃、聚苯醚、弹性体、分散剂 中图分类号：TB324，TQ334 文献标识码：A Research and Applications of YY-503 in Halogen-free Flame Retardant PPO/SEBS Blend Yang Fanwen1, Tan Minghao1, Zhang Liang1, Xu Kemou2 (1. Department of Biomedical Engineering, Guangzhou Medical University, Guangzhou 510182, China; 2. Guangzhou Yuantai Synthetic material Co. Ltd., Guangzhou 510665, China) Abstract: The effect of multifunctional additive YY-503 on tensile strength, blending performance, rheological properties, surface gloss and flame retardant properties PPO/SEBS elastomer is studied . With increase of the YY-503 content, the tensile strength and elongation of elastomer first increases then decreases. Notched impact strength and surface gloss of elastomer sequentially increase. When the content of YY-503 is 0.5 to 1%, the flame retardant properties meet the V-0 standard, surface gloss increase 20% and L value increases 3 based. The heat resistance of YY-503 is excellent. The interfacial bonding strength between magnesium hydroxide and plastic matrix is improved by adding YY-503 as modifier, which can reduce the friction between the polymer and Mg(OH)2 and avoid the degradation and yellowing of blends which are caused by higher shear stress. Keywords: halogen-free flame retardant; polyphenylene oxide; elastomer; dispersant 1 引 言 普通高分子材大多数可燃、容易引发火灾,在应用过程中存在着极大的安全隐患,严重威胁人民群众生命和财产安全[1]。传统聚氯乙烯（PVC）材料制备的电线电缆包覆材料含有大量的增塑剂和卤素，燃烧时释放出大量的烟雾和毒气, 危害人体健康，严重时使人窒息死亡[2]。随着欧盟 RoHS 指令的颁布实施和人们环保意识的加强，PVC电缆料的应用越来越受到限制。因此,开发新型耐高温柔性无卤阻燃电缆料是防止和减少火灾事故的战略性措施之一,具有重要的理论和实际意义。 聚 2,6-二甲基-1,4-苯醚(PPO)是一种主链上含有苯环的非极性线型高分子材料, 具有良好的力学性能、耐热性能和阻燃性