不锈钢光亮退火炉装备和工艺研究 　　摘 要：根据相关的不锈钢BA板处理技术，对关键装备光亮炉的不同炉型，进行对比、分析。从炉体结构、保护气氛控制、加热及冷却方式和工艺操作等角度，全面分析、总结了三种不同炉型：立式马弗加热炉、立式电加热砌砖炉和立式电磁感应加热炉的特点和优劣；同时对实际生产运行过程中的存在的问题和操作特点进行讨论。得出不同炉型的控制关键点、提出有效的控制和操作方案，对生产有借鉴之处。 关键词：不锈钢光亮退火马弗电磁感应保护气氛露点 Analysis of Bright Annealing Furnace Equipment And Process Gao Jianbing Abstract This article focuses on the comparative analysis of different bright annealing furnace, according to related stainless steel bright annealing technique. Advantages and disadvantages for the 3 furnaces (vertical muffle furnace, vertical electrical heating brick furnace and vertical electromagneticheating furnace) are concluded by analyzing the furnace structure, protection atmosphere control, heating and cooling style and process operations. Meanwhile key control points are summarized via discussing the problems in actual production operation, which can provide guidance for production. Key words Stainless steel; Bright annealing; Muffle; Electromagnetic introduction; Protection atmosphere; Dew point 中图分类号：TF764+1 文献标识码：A 随着不锈钢BA板产品广泛应用和冶金装备、工艺技术的不断进步， BA板生产的光亮炉得到了很快的发展。光亮炉作为不锈钢光亮退火的关键装备有很多的优点，钢带在保护气氛中实现退火不产生氧化，产品质量高、不产生酸烧损同时不污染环境。 目前，世界上比较流行的大型立式光亮退火炉有全马弗加热炉、砌砖电加热炉和电磁感应加热炉三种炉型。根据加热方式的不同一般分为电加热、燃气加热及电磁感应加热。本文对这三种炉型的结构、气氛控制和工艺操作进行分析、对比，并结合实际生产进行讨论。 1.立式马弗光亮炉 1.1布置结构 通常采用加热段在下、冷却段在上的上行加热方式，典型的全马弗光亮退火炉主要由进口密封室、马弗加热段、辐射冷却段、喷气冷却段、辊顶室、下降通道、出口密封室组成。 入口密封室（图1）为密封辊密封，整个箱体充氮气，内装弹跳辊保证炉内带钢张力稳定，辊面包橡胶。马弗管和入口密封室之间通过油封方式连接，整体柔性吊挂在马弗管下。油封连接（图2）能很好适应马弗高温蠕变伸长并保证炉内气体密封。此种方式结构不容易发生着火。 图1：含弹跳辊的密封结构 图2：含弹跳辊的密封结构 加热段的马弗管是立式圆锥薄壁体结构，由于各生产线的产量不同，马弗长度也不同，一般其最大长度约28m左右，直径约1800mm左右，厚度：从上到下为22mm～10mm。马弗采用耐高温的高镍合金钢，其材质一般为INCOLOY 600系合金，马弗底部采用油封结构，马弗采用吊挂的方式和冷却段连接，法兰采用水冷结构。 马弗的寿命，不同的公司设计的炉温和选用的马弗材质各不相同，因此马弗的使用寿命也各不相同，一般为2～5年。 加热燃烧室（图3）外形结构为圆柱体，内衬耐火陶瓷纤维，一般采用天燃气作为炉子燃料，利用低NOx高速烧嘴给马弗管加热，所配置烧嘴的个数依据产量而定。燃烧室温度一般为1150℃ 左右。通过先加热马弗管来间接加热带钢，马弗罩内为保护气氛。马弗罩最高耐温1150℃,炉温一般控制在1100℃-1150℃，热效率为50-55%。 图3：加热燃烧室示意 辐射冷却段为方形钢结构，内衬隔热材料，外壁挂蛇形冷却水管，水管不和保护气氛接触，水管漏水不影响气氛