转炉汽化冷却烟道破损因素分析及改进措施 ·1 · 转炉汽化冷却烟道破损因素分析及改进措施 樊 译 石 焱 胡长庆 张玉柱 冯英英 （华北理工大学冶金与能源学院，河北省现代冶金技术重点实验室，河北唐山 063000 ） 摘 要 本文分析了周期性交变热应力、水循环不均匀、水质、结渣、炉尘冲刷等因素对转炉汽化冷却烟道的影响， 并提出通过保持自然循环最小流量、严格控制补给水水质、合理控制烟气流速、改善水冷管材质、完善烟道结构设 计，以及开展汽化冷却烟道烟道破损机理研究，优化水冷管相关参数等有效改进措施，提高转炉汽化冷却烟道寿命。 关键词 转炉，汽化冷却烟道，破损，寿命 Damage Factor Analysis And Improvement Measures of Converter Vaporization Cooling Flue Fan Yi, Shi Yan, Hu Changqing, Zhang Yuzhu, Feng Yingying (North China University of Science and Technology, College of Metallurgy and Energy, Hebei Key Laboratory of Modern Metallurgy Technology, Tangshan Hebei 063000, China) Abstract This article describes the cycle of alternating thermal stress, uneven water cycle, water quality, slagging, furnace dust flushing and other factors that affect the lifetime of converter vaporization cooling flue, and summarizes to keep the minimum natural cycle flow, control the water quality strictly, control of the flue gas flow rate reasonable, improving the water-cooled pipe material, improve the flue structure design and carry out research on vaporative cooling flue broken mechanism, optimize the relevant parameters of the cooling tube, improve the lifet of converter vaporization cooling flue. Key words converter, vaporative cooling flue, damage, lifetime 1 引言 转炉汽化冷却烟道是参与转炉炼钢过程的重要设备之一，负责将炼钢过程产生的烟气进行回收并进行冷 却、净化，以达到回收利用的目的。汽化冷却烟道包括：活动烟罩、炉口固定段烟道、可移动段烟道、中间 段烟道和末段烟道五部分。转炉烟道长期处于高温、多尘、高压的环境。当位于可移动段的氧枪进入转炉开 始吹炼时，大量的高温烟气穿过烟道，使烟道热负荷急剧增加；相反，吹炼停止，氧枪提起时，烟道的热负 荷急剧减小。这种周期性、急剧性的运行工况下，热负荷的波动十分频繁，导致汽化烟道的使用环境恶劣， 从而影响汽化烟道的使用寿命。根据实际情况来看，转炉汽化冷却烟道寿命较低，活动烟罩的平均使用寿命 只有4～12 个月，炉口段及斜段烟道的首次爆破时间也只有2～3 年，经常出现水冷管爆管、漏水现象，严 重影响炼钢生产的经济性和安全性。然而，长期以来，以事后修补为主的方法无法从根本上解决其破损问题。 因此，从转炉汽化冷却烟道运行状况入手，分析水冷管破损原因，提出改进措施，将有助于转炉汽化冷却烟 道破损机理研究，对提