转炉溢渣喷溅控制与研究.pdfVIP

转炉溢渣喷溅控制与研究 吕长海1,2) 程树森1) 杨燕春2 ） (1. 北京科技大学冶金与生态学院, 北京100083 ;2. 山东莱钢永锋钢铁有限公司, 山东齐河251100) 摘 要 本文论述了溢渣喷溅形成的原因，对喷溅时渣子的各组分含量进行分析，阐述了溢渣与喷溅的形成同加料时机、枪 位、氧压、C-O反应的程度等有直接的关系，对炉渣取样情况进行了详细分析。取样化验发现，喷溅渣中含有大量的粒铁，全 铁含量也相对终点渣样偏高，针对此情况制定了相应的溢渣与喷溅控制措施。 关键词 溢渣；喷溅；粒铁；全铁；喷溅渣 分类号 Overflow of converter slag splashing control and research 1,2) 1) 2) LV Chang-hai , CHENG Shu-sen ,YANG Yan-chun 1) Beijing university of science and technology institute of metallurgy and ecology, Beijing 100083; 2) Shandong laiwu yong feng steel co., LTD., shandong QiHe 251100). ABSTRACT Pick to the paper discusses the formation cause of overflow slag splashing, the splash of pulp are each component content analysis, this paper expounds the formation of overflow slag and splash with charging time, gun, oxygen pressure, C - O reaction degree has a direct relationship, and the sampling conditions are analyzed in detail. Sampling tests found that splash slag containing large amounts of iron, total iron content is relatively high end slag samples, for this situation made the corresponding overflow slag and splash of control measures. KEY WORDS slag overflow; Splash. Grain of iron; All the iron; Splash slag 转炉炼钢的根本就是要控制好过程渣的状态和过程温度，造渣是转炉炼钢过程的关键环节, 控制造好 渣是提升转炉炼钢水平的前提,在吹炼过程中形成良好的炉渣，能有效去除钢水中的有害元素，如：S、P等, 以此来提升钢的品质。吹炼过程的造渣原则应遵循“初期渣早化, 过程渣化好, 终渣化透”。 目前,转炉造渣操作的辅助手段有：烟气分析、音频化渣、炉口火焰热成像等，通过计算转炉中的氧累 计情况及CO气体产生量，来进行喷溅预报。通过对转炉冶炼过程中炉气CO浓度变化的研究, 提出利用CO 浓 度曲线来指导转炉造渣操作和枪位控制的方法。 1 取样转炉基本状况 60吨顶底复吹转炉，生产钢种主要为三级建筑用钢、出口建材钢，转炉炼钢主要采用人工拉碳控制终 点出钢，无任何辅助终点控制设备，冶炼过程中时常出现溢渣喷溅等情况。 2 转炉溢渣喷溅形成原因 目前, 喷溅和溢渣形成机理不很明确, 尚无统一定论。 研究认为, 氧气顶底复吹转炉在吹炼过程中, 早化渣和化好渣至关重要