熔渣对镁碳耐火材料的腐蚀增加碳含量的影响.docVIP

熔渣对镁碳耐火材料的腐蚀增加碳含量的影响 THE INFLUENCE OF CARBON CONTENT ON THECORROSION OF MGO-C REFRACTORY MATERIALCAUSED BY ACID AND ALKALINE LADLE SLAG This paper describes an investigation of the influence of increasing carbon content on the corrosion of MgO-C refractory material by molten slag. The refractory material contained mass fraction of 98 % MgO, approximately 2 % Fe2O3, and graded quantities from 3 % to 18 % C. The corrosion was investigated in melts of reduction ladle slags at a temperature of 1600 °C in laboratory conditions. A sample of refractory material with dimensions of 10 × 10 × 100 mm