碳纤维布加固损伤混凝土梁的抗剪疲劳试验-武汉理工大学学报.PDFVIP

27 7 武 汉 理 工 大 学 学 报 Vol. 27 No. 7 2005 7 JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY Jul. 2005 刘沐宇, 骆志红, 刘其卓 ( , 430070) : 对钢筋混凝土受剪梁疲劳损伤后进行了粘贴U 型碳纤维布加固钢筋混凝土损伤梁的疲劳试验试验结果 明: 钢筋混凝土梁粘贴U 型碳纤维布后箍筋应变减小了20% ~ 40% , 斜裂缝宽度减小了34% ~ 39% , 且碳纤维布用量越 大效果越明显因此, 粘贴碳纤维布可以较大提高损伤混凝土梁的抗剪疲劳性能, 延长损伤混凝土结构的使用寿命 : 碳纤维; 加固; 抗剪; 疲劳试验; 损伤 : TU 32/ 399 : A : 1671-4431(2005)07-0054-03 Shear Fatigue Performan e of Damaged RC Beams Strengthened with CFRP Sheets L I U M u-y u , L UO Zh i-hong , LI U Qi-z huo (School of ivil Engineering and Architecture, Wuhan University of Technology, Wuhan 430070, hina) Abstra t: The damaged R beams strengthened with carbon fiber-reinforced plastic ( FRP) sheets of U-wraps w ere tested in shear fatigue after these beams w ere damaged in fatigue. The experimental results indicated that after strengthened with FRP sheets of U-w raps, the stresses of stirrup was decreased by 20% ~ 40% , the w idth of diagonal crack was decreased by 34%~ 39% , and the larger amount of FRP sheets, the more significant this effect was. The test show ed that externally bonded FRP sheets of U-w raps can improve the shear fatigue performance and increase the fatigue life of reinforced concrete beam significantly. Key words: carbon fiber reinforced plastic( FRP) ; strengthen; shear; fatigue test; damage [ 1~ 3] , [4~ 5] , , [ 6] 1 1. 1 , b @ h = 100 mm @ 160 mm, L = 1 200 mm, l = 1 000 mm, 30, 39.5 MPa, 28 d 1, L200- , 0. 111 mm, 4 053 MPa, 212 GPa, YZJ- U + (2) :2005-03-04. : ( 2002A