相变储能加气混凝土砌块性能研究.pdf

学兔兔 全国中文核心期刊 新 建巍粉 相变储雒力口号混凝土砌=l[夹的牲雒研究 刘平，沈新元，万泽青 (扬州大学 建筑科学与工程学院，江苏 扬州 225009) 摘要：将有机相变材料硬脂酸丁酯浸渍到加气混凝土砌块中，利用其相变特性和砌块的保温效果，制成一种新型墙体材料。用 对比试验的方法，测试了该种墙体材料的智能调温、强度等性能。结果表明，该新型墙体砌块具有良好的保温调温性能。 关键词：相变材料；硬脂酸丁酯：加气混凝士砌块：浸渍 中图分类号：TU522．3+2 文献标识码：A 文章编号：1001—702X(2010)12—0026—03 Experimental research on PCM aerated concrete blocks LIU ，SHEN Xinyuan，WAN Zeqing (College of Civil Science and Engineering of Yangzhou University，Yangzhou 225009，Jiangsu，China) Abstract：Butyl stearate is a kind of organic phase change material(PCM)．A kind of novel walling building block is prepared by impregnating butyl stearate into aerated concrete blocks to make use of its phase—change performance and thermal preservation effect．The properties of intelligent thermoregulation and compressive strength were studied by comparative experiments． Research results show that the new PCM walling building blocks have good thermal insulation and thermoregulation properties． Key words：phase change material；butyl stearate；aerated concrete block：impregnation 对其综合性能进行研究。 O 引 言 1 PCM墙体砌块制作 随着现代建筑逐步向高层发展，围护结构所用材料多改 为轻质材料，但普通轻质材料热容较小，外界温度变化时导致 1．1 试验材料 室内温度波动较大，这不仅影响室内热环境，而且还增加了空 采用江苏荣能集团有限公司生产的粉煤灰加气混凝土砌 调负荷，导致建筑能耗上升。解决该问题的有效方法之一就是 块，尺寸为100 mmxl00 mmxl00 mm，干密度0．5—0．8 m3，抗 采用蓄热技术[11。通过向普通建筑材料中加入相变材料 压强度不小于4 MPa，其质量轻，强度高，保温性能、耐水性、耐 (Phase Change Material，PCM)，可以制成具有较高热容的相 冻性及耐久性好，是扬州地区大量使用的一种建筑砌块。 变储能建筑材料，已成为目前国内外研究的热点[2-3]。