太阳能铝浆触变性研究.doc

本 科 毕 业 论 文题 目 作 者： 专 业： 高分子材料与工程 指导教师： 完成日期： 摘要 本课题主要研究各种触变剂对太阳能铝浆触变性的影响，通过改变有机粘结剂的配方来调整铝浆的触变性。实验结果表明：添加型触变剂聚酰胺蜡、氢化蓖麻油，氧化聚乙烯蜡和溶剂型触变剂柠檬酸三丁酯、邻苯二甲酸二丁酯的含量分别为1.4%、1.4%、1.7%、9%、8%时铝浆的延展直径为54mm，渗漏克重为0g，触变性最好。而氧化聚乙烯蜡和柠檬酸三丁酯混用时，可以改善触变性，如在加入5%柠檬酸三丁酯的情况下，氧化聚乙烯蜡的含量为1.4%时铝浆的延展直径为54mm，渗漏克重为0g，触变性最好。因此，触变剂的种类和含量对铝浆触变性有重要的影响。添加型触变剂聚酰胺蜡、氢化蓖麻油触变效果好些，溶剂型触变剂邻苯二甲酸二丁酯效果好。 关键词：铝浆、触变性、触变剂、机粘结剂 ABSTRACT The effect of various thixotropic agent on the thixotropy of solar aluminum paste was researched in this paper. The thixotropy of aluminum paste was changed by changing the content of organic binder.Experimental results show that with the increase of thixotropic agent,:the thixotropy was improved. When the amount of adding thixotropic agent was 1.4%, and solvent-based thixotropic agent was 8%, , the extending diameter of aluminum paste was 54mm,and leakage grams of weight was 0 g,and then the thixotropy was best.The thixotropy was improved if oxidized polyethylene wax and citrate worked together. For instance,in the case of 5% tributyl citrate, the amount of polyethylene wax was decreased Key words:.aluminum paste, thixotropy, thixotropic agent , organic binder  目录 第一章 综述 3 1.1光伏材料概述 3 1.1.1光伏材料背景 3 1.1.2晶体硅太阳能电池工作原理 3 1.1.3太阳能电池的生产工序 4 1.2电子浆料 5 1.2.1 电子浆料简介 5 1.2.2 电子浆料的组成 5 1.3铝浆 7 1.3.1铝浆概述 7 1.3.2.铝浆的组成 7 1.4 触变剂的种类 8 1.5 触变性 8 1.5.1 触变性定义 8 1.5.2 触变剂的作用 8 1.5.3触变性的测定方法 9 第二章 实验部分 10 2.1 实验原理 10 2.2 实验原料与设备 10 2.2.1实验原料 10 2.2.2 实验仪器 11 2.3 试验流程 11 2.3.1 铝浆的制备 11 2.3.2 聚酰胺蜡对太阳能铝浆触变性影响 12 2.3.3溶剂网络型触变剂对太阳能铝浆触变性的影响 12 2.3.4 复配触变剂对太阳能铝浆触变性影响 13 第三章 结果与讨论 14 3.1 聚酰胺蜡对铝浆触变性的影响 14 3.2氢化蓖麻油的量对太阳能铝浆触变性的影响 14 3.3 氧化聚乙烯蜡的量对太阳能铝浆触变性的影响 15 3.4 柠檬酸三丁酯量对太阳能铝浆触变性影响 16 3.5 邻苯二甲酸二丁酯的量对太阳能铝浆触变性的影响 17 3.6 复配触变剂对太阳能铝浆触变性的影响 17 第四章 结论 19 参考文献 20 致 谢 21 第一章 综述 1.1光伏材料概述 1.1.1光伏材料背景 光伏发电是利用光电效应，使太阳光辐射能转变成电能的发电方式，是当今太阳光发电的主流。太阳光发电是无需通过热过程直接将光能转变为电能的发电方式，它包括光伏发电、光化学发电、光感应发电和光生物发电。光伏效应就是当物体受到光照射时， 物体内的电荷分布状态发生变化而产生电动势和电流的一种效应。后来有人发现当太阳光或其他光照射半导体的PN结时，就会在PN结的两边出现电