锂离子电池负极材料ZnO_CoFe2O4制备及其电化学性能研究-本科毕业论文.docxVIP

锂离子电池负极材料ZnO/CoFe2O4的制备及其电化学性能研究摘要：本文采用简单易行的水热种子法来制备ZnO/CoFe2O4，运用了XRD，SEM和电化学工作站等测试手段研究了ZnO/CoFe2O4的结构、形貌、以及电化学性能。XRD和SEM结果显示ZnO/CoFe2O4颗粒尺寸分布均匀，颗粒粒径为100nm,晶体形貌较好。循环伏安法表明在100 mA/g的电流密度下，ZnO/CoFe2O4复合材料首次嵌脱锂容量分别为1194 mA·h/g和715 mA·h/g，首次库伦效率为71.4%。50次循环后仍具有793 mA·h/g的可逆容量，且库伦效率达到98%以上。该测试说明ZnO/CoFe2O4有较好的比容量和循环稳定性。关键词：水热种子法；电化学性能；ZnO/CoFe2O4；锂离子电池Synthesis and Electrochemical Performances oflithium-ion battery anode material of ZnO/CoFe2O4Abstract:This article reports on a more simple method which is to compound ZnO/CoFe2O4by using hydro-thermal seed method. Thestructure，morphology and electrochemical performance of ZnO/CoFe2O4 were investigated by XRD, SEM and Electrochemical workstation .The XRD and SEM pattern show that the homogeneous particle sizes of ZnO/CoFe2O4 nanoparticles are got. The crystallitesare about 100 nm, the crystal morphology is great. Cyclic voltammetry results exhibit that at a current density of 100 mA/g, the ZnO/CoFe2O4 delivers a lithiation capacity of 1194mA·h/g and a delithiation capacity of 715mA·h/g in the initial cycle, corresponding to a coulombic efficiency of 71.4%. After 50 cycles, it still has a reversible capacity of 793mA·h/g, which maintains98% of initial charge capacity. Test results show that the ZnO/CoFe2O4electrode has the great capacity and cycle stability .Key Word：hydro-thermal Seed Law; electrochemical properties;ZnO/CoFe2O4; lithium-ion batteries.目录摘要I关键词IAbstractIIKey WordII1.前言11.1研究背景11.2锂离子电池工作原理21.3锂离子电池的结构及设计原理31.4锂离子电池负极材料41.5本文的选题意义102.实验102.1实验药品102.2实验仪器112.3电极材料的合成112.4电池的制备123.结果与讨论123.1X射线衍射仪123.2扫描电子显微镜143.3电化学性能测试164.结论17参考文献18致谢211.前言1.1研究背景21世纪科技高速发展的今天,地球上原本储存量就非常有限的能源随着人类无节制的开发使用变得越发的稀少 ,而在我国由于人口过多,能源短缺相对来说更加的严峻,随着能源消耗的增长,开发利用新能源是我们的当务之急,化学能源与能源的关系越来越紧密,化学电源又称电化学电池,它能够通过一系列反应将化学能转换为人们需要的电能 [1-2]。我国电池生产量及需求一直处于国际前列,但是在电池研发和创新方面一直不尽如人意。因此,在电池面临大发展机遇和严峻挑战的今天,自主创新是最好的出路。表1不同类型二次电池性能参数比较电池种类功率密度/(W?h/kg)能量密度/(W?h/kg)单元电压/V循环寿命/次成本/[$/(kW?h)]环境保护铅酸电池200～30035～402.0300～50075～150污染镉镍电池150～35040～601.2500～1000