TC4钛合金电子束冷床熔炼成分均匀性研究.pdfVIP

Metallurgical Engineering 冶金工程, 2014, 1, 28-34 Published Online March 2014 in Hans. /journal/meng /10.12677/meng.2014.11005 Research on Composition Uniformity of TC4 Alloys during Electron Beam Cold Hearth Melting Lei Luo1,2, Xiaonan Mao1,2, Guanjun Yang2 1 School of Metallurgy Engineering, Xi’an University of Architecture and Technology, Xi’an 2 Titanium Alloy Research Centre, Northwest Institute for Non-Ferrous Metal Research, Xi’an Email: luolei0301@126.com th th th Received: Feb. 24 , 2014; revised: Mar. 7 , 2014; accepted: Mar. 18 , 2014 Copyright © 2014 by authors and Hans Publishers Inc. This work is licensed under the Creative Commons Attribution International License (CC BY). /licenses/by/4.0/ Abstract The composition uniformity of TC4 alloys ingot during electron beam cold hearth melting which used different melting speeds was studied. The results show that the ingot produced by electron beam cold hearth melting accord with the national standard, with a good melting effect. In the axi- al direction of the ingot from the top to the bottom, the Al content presents a decrease trend, and as the melting rate decreases, the decrease trend is more evident. The V element distribution is uniform, and no segregation phenomenon appears. In the radial direction of the ingot, the alloy elements distribution is very uniform. Keywords EBCHM; TC4 Alloys; Composition Uniformity; Segregation TC4钛合金电子束冷床熔炼成分均匀性研究 1,2 1,2 2 罗 雷 ，毛小南 ，杨冠军 1西安建筑科技大学冶金工程学院，西安 2西北有色金属研究院钛合金研究所，西安 Email: luolei0301@126.com 28 TC4 钛合金电子束冷床熔炼成分