模具钢新型钢种的开发和研究.docVIP

1 - 模具钢新型钢种的开发和研究 马绍华 储少军 季爱兵 （北京科技大学 冶金与生态工程学院 100083） 摘要：本文论述了模具钢的生产工艺现状及其市场供需状况，指出了现有模具钢系列钢种在生产和使用过程中存在的问题和不足。提出了新一代含氮模具钢的开发与研究方向，其中研究内容包括：冶炼、锻造和热处理工艺的研究。新一代含氮模具钢的研究既提高了模具钢的疲劳寿命，又降低了生产成本，具有广阔的市场前景。 关键词：含氮模具钢、疲劳寿命、研究与开发 The development and research of the new generation die-steel Ma Shaohua Chu Shaojun (School of Metallurgical and Ecological Engineering University of ScienceTechnology Beijing 100083) Abstract: This paper describes the process technique and the requirement of the market of the die- steel, tell us the defect in the application. The content which we develop an research in the new generation nitrogenous die-steel is that: melt、forge、heat-treatment. The application of the new generation nitrogenous die-steel can prolong the fatigue life time and the cost reduction. So the new generation nitrogenous die-steel can have a wide market foreground. Key Words: nitrogenous die-steel、fatigue life time、research and development 联系人：马绍华(1965—)，在读博士生，主要从事高氮奥氏体不锈钢的研究，电话：01062332790，E-mail：mshwxq@126.com. 模具钢的发展和现状 模具钢的生产和制造是衡量现代模具整体技术水平的指标，也是模具工业发展中不可忽视的重要环节。随着模具需要量的急剧增加，模具制造业已经逐步发展成为一个独立的行业，而且其发展速度领先于其他行业[1]。所以国际上提出：“模具是工业发展的基石”，“模具是促进社会繁荣的动力”。 模具钢的简介 根据模具工作条件的不同，将模具钢分为三类，即冷作模具钢、热作模具钢和塑料模具钢。 1、冷作模具钢是用于制造冷冲模、冷镦模、冷挤压模、拉丝模、滚丝模等类型的模具，冷作模具钢的含碳量较高，大部分属于过共析钢或莱氏体钢，经最终热处理后具有较高的硬度和耐磨性。目前世界上通用的冷作模具钢可分为三种类型： 1)低合金冷作模具钢：以美国的ASTM A681标准中的O1（9CrWMnV）和O2（9Mn2V）为代表； 2)中合金冷作模具钢：以美国的ASTM A681标准中的A2钢（Cr5MoV）为代表； 3)高碳高铬型冷作模具钢：以美国的ASTM A681标准中D2（Cr12Mo5V1）和D3（Cr12）为代表。 2、热作模具钢主要用于制造热锻模、热挤压模和压铸模等。热作模具钢的含碳量一般在0.30~0.60%范围内，属于中碳钢，在使用过程中具有较高强度，较高的韧性以及足够的冷热疲劳强度等。目前世界上用量最大的三类通用型热作模具钢为： 1)低合金热作模具钢：代表性的钢号为5CrNiMo（V）、5CrMnMo等； 2)中合金热作模具钢：这类钢为铬系热作模具钢，代表性的钢号H13（4Cr5MoSiV1）、H11（4Cr5MoSiV）等； 3)高合金热作模具钢：应用最广的传统的热作模具钢，代表性的钢号H21（~3Cr2W8V）。 3、塑料模具钢是近十年来发展起来的新型钢种，此类型钢种类繁多，用途极广。由于塑料模具钢的工作环境和使用性能要求，钢中含碳量较低，合金成分较低，为了达到其使用性能，对塑料模具钢的纯洁度要求十分苛刻，成品模具呈镜面状态，尺寸朝宽厚板方向发展。塑料模具钢目前分为5类： 1）非合金型：主要采用中碳结构钢，以日本的S55C为代表； 2）预硬型：一般采用中碳合金钢，以美国的P20钢为代表； 3）时效硬化型：此类钢在低、中碳合金钢中，通过加入通过Ni、Al、Ti、Cu等元素，淬火后