以双裂缝试验量测胶结石膏II型破裂韧度之研究.PDFVIP

以雙裂縫試驗量測膠結石膏II型破裂韌度 之研究* The Measurement of the Mode II Fracture Toughness of Adhesive * Gypsum Using Short Beam Compression Test 1 2 1 3 1 2 1 3 S.H. Wang J.W. Tsai C.H. Chen C.L. Wang Th i s st u dy at t empt s t o m ea su r e th e Mode I I () (sliding mode) fr act u r e t ou gh n ess of gyp su m an d (3 1) (1 1) adhesive gypsums u sing the short beam compression (POLY) II t est (SBCT) and t o evalu at e the cir cu m st ances for cr ack r ep air ing . Th e th r ee adh e sive gyp su m s ar e Gyp sum-Epoxy (3:1), Gyp sum-Epoxy (1:1), Gyp sum- un satu r at ed Polyest er Resin (POLY ). The Mode II fracture toughness was measured with SBCT under lateral con finement s and varying crack separation s. 0.1~0.250.4 Results showed that the testing condition is favorable for Mode II fracture toughness when the separation r atio is b etween 0.1 and 0.25. When the sep ar ation r atio exceeds 0.4, the fr acture condition will resu lt in an u n de sir able t en sile failu r e . Th e in cr ea se in confining stress decreases tensile stress on the slot tip II thereby favorable for Mode II fracture. This study also showed that the POLY adhesive gypsum has the best response under confining condition . A finite element AN SY S package AN SYS was u sed to develop the correlation equation for the critical stress intensity factor (fracture toughness). 關鍵字：