热处理制度下ti6242s及ti6242显微组织与性能关系的分析-材料加工工程专业论文 word格式.docxVIP

Research of Relationship between microstructure and properties for Ti6242S and Ti6242 alloys at different heat treatmentSpecialty:Materials Processing Engineering Name:Liu JunInstructors:Yang GuanjunMao XiaonanAbstractIn the paper, high temperature titanium alloys of Ti-6242S and Ti-6242 are studied, which microstructures is quantitatively demarcrated by Image-Pro-Plus6.0 software. Through room temperature tensile test and high temperature tensile test, the paper systematically studied the relationship between microstructure and properties of the different heat treatments, and discussed effect Si on tensile mechanical properties. Finally, the relationship between parameters and microstructure was obtained initiallyby data analysis methods. The results are as follows：⑴.Heat treatments under cooling mode have been shown: when solution temperature is 970℃, water-quenched could create martensite α′ phase, and itsstrengthening effect is better than influence of air-cooled (AC) and furnace cooling (FC). After aging treatment, martensite α′ phase decompose, the strength of alloys is highest, plastic is lowest. On the contrary, furnace cooling produce a litter α phase, the strength of alloys is the lowest, the plastic is the better. The combing properties of alloys air cooled are better than that of alloys water quenched and furnace cooled.⑵.Different parameters of heat treatments have been shown: At different solutiontemperature, contents and sizes of equiaxed α phase and lath α phase have a significant change, which ultimately result in diffences of mechanical properties. Other researches of heat treatment paraments containing solution time, aging temperature and aging time indicate varation of mechanical properties results from the chang of microstructure paraments. There is a phenomenon of dissolution under conditions of changes of three heat treatment paraments, in which contents of equiaxed α phase decrease, and contentsof lath α phase increase.⑶.High temper