超声法制备NdFeB薄膜电化学性研究.doc

毕业设计（论文） 题 目 超声法制备NdFeB薄膜的电化学性研究 化学工程系 专 业 化学工程与工艺 班 级 学生姓名 学 号 指导教师 职 称 讲师 二〇一六年五月三十日 超声法制备NdFeB薄膜的电化学性研究 本文对超声波条件下的沉积NdFeB合金镀层进行了研究。通过改变镀液成分及镀工艺参数，得出它们对合金镀层沉积速度、电化学性能、化学成分、组织形貌和磁学性能的影响。并采用电化学阻抗 (EIS)、循环伏安以及恒电位阶跃等方法对钕铁硼电化学沉积初期过程中的电化学行为进行了研究。通过测试和分析可得出，钕铁硼合金在较好的共沉积条件下，成核机制为3D瞬时成核/生长。Ultrasound of NdFeB film prepared by the chemical research Abstract In this paper, the ultrasonic electrodeposition under the condition of NdFeB alloy coatings were studied. This experiment by changing the composition of plating solution pH and electroplating process parameters, and in the process of electroplating to ultrasound. To obtain the alloy coating deposition rate, the electrochemical properties, chemical composition, morphology and magnetic property. And (EIS), cyclic voltammograms and electrochemical impedance methods such as constant current status jump on the electrochemical behavior of ndfeb early electrochemical deposition process was studied. Choosing the way of ultrasonic generator directly ACTS on the plating solution and study the effects of ultrasound on the structure and properties of coating. Through test and analysis can be concluded that ultrasonic intervention has greatly increased the deposition rate, and ndfeb alloy under the condition of good codeposition, nucleation mechanism for 3D instantaneous nucleation/growth. Key words :NdFeB; electrochemical properties; Electroplating; Magnetic thin film 引言 当代磁性材料发展以永磁材料为主，主要是铁氧体、AlNiCo、稀土永磁三大类。稀土永磁材料的发展总共经历了三代，第一代是1976年问世的SmCo5稀土永磁材料，第二代为70年代发现的SmCo17稀土永磁材料，第三代即为以其高磁能积、高矫顽力和高能量密度而被大众熟知的钕铁硼稀土永磁材料。优良的性能和较高的性价比居于稀土磁性材料中的核心地位，且被称为“磁王”NdFeB永磁材料KJ·m-3 (64MGOe)[1, 2]，成为了代替钐钴永磁的理想替代品。而且已被广泛应用于现代工业和电子工业，尤其是电器、电磁分离电机市场，硬盘存储材料、NMR（核磁共振）等。[3]。超声波除了能够改善传统电镀工艺过程中存在的液相传质慢、电流密度低等问题，还可以提高镀层与基底的结合力，改善镀层的粗糙度[4, 5]。其次，在电镀沉积过程中加入超声波，能够明显地提高镀层活性，很大程度地降低了薄膜的矫顽力。本文通过改变镀液成分、化学镀工艺参数及添加稀土，并在制备NdFeB磁性薄膜过程中加入超声波，比较沉积速度、电化学性能、组织结构、成分形貌和磁学性能，通过分析得出制备效率和综合性能优异的薄膜材料。 第一章 绪论 1.1稀土电沉积简介 根据电沉积制备稀土元素合金所采用的体系的不同，