铁酸盐纳米材料的制备及其性能研究 摘要 通过比较不同的制备方法,选用聚合物配位法制备纳米铁酸锌、镍锌铁氧体，水合肼还原法制备镍锌铁氧体负载Cu2O粉体、并利用XRD，FTTR对制得的纳米铁酸锌、镍锌铁氧体负载Cu2O粉体、铁酸镍锌进行表征。以镍锌铁氧体负载Cu2O粉体为光催化剂,对甲基橙溶液进行光催化氧化降解,考察镍锌铁氧体负载Cu2O粉体在紫外光源下的光催化效果。结果表明对于浓度为20mg/L的甲基橙溶液,当催化剂与甲基橙溶液的固液比为2g/L时,紫外线辐照2h后,降解率能够达到92.57%。另外,重复使用催化剂两次之后,其光催化降解率仍能达到可观的效果。 关键词: 铁酸锌 镍锌铁氧体负载Cu2O 光催化降解 Abstract By comparing different preparation methods, the choice of coordination polymers were prepared nanoscale iron zinc, nickel zinc ferrite load Cu2O powder, nickel zinc ferrite.Using X-ray diffraction XRD, infrared FTTR of nano zinc ferrite prepared, nickel zinc ferrite load Cu2O powder, nickel zinc ferrite were characterized.Cu2O nickel zinc ferrite powders as photocatalyst loading on methyl orange photocatalytic degradation were investigated nickel-zinc ferrite powder load Cu2O under different light sources in the photocatalytic effect.The results show that for a concentration of 20 mg / L of methyl orange, methyl orange as the catalyst and the solid-liquid ratio of 2g / L, the UV radiation 2 h, the degradation rate can reach 92.57%.In addition, repeated several times using the catalyst after the photocatalytic degradation rate is still able to achieve significant results. Key words: zinc ferrite Nickel zinc ferrite load Cu2O photocatalytic degradation 目录 摘要 I Abstract II 第一章 前言 1 1.1制备铁酸盐纳米材料的意义 1 1.2铁酸盐纳米材料的制备方法 1 1.2.1 溶胶一凝胶合成法 1 1.2.2 水热法 2 1.2.3 机械化学合成法 2 1.2.4 共沉淀法 3 1.2.5 冲击波合成法 3 1.2.6 低温燃烧合成法 4 1.2.7 喷雾热分解法 4 1.3铁酸盐纳米材料的研究前景 5 1.4铁酸锌的性质 5 第二章 实验部分 7 2.1实验药品 7 2.2试验仪器 7 2.3样品制备 7 2.4试验方法 7 2.4.1 ZnFe2O4纳米材料的制备方法 7 2.4.2铁酸镍锌纳米材料的制备 9 2.4.3镍锌铁氧体负载Cu2O粉体的制备 11 2.4.4镍锌铁氧体负载Cu2O粉体的光催化应用实验步奏 11 第三章 结果与讨论 12 3.1铁酸锌纳米材料的表征及讨论 12 3.1.1红外光谱分析 12 3.1.2热解产物的XRD分析 13 3.1.3粉体的比表面积 15 3.2铁酸镍锌纳米材料的表征及讨论 17 3.2.1 红外光谱分析 17 3.2.2热解产物的XRD分析 18 3.2.3热解产物的磁性能 18 3.2.4前躯体的外貌 20 3.3 镍锌铁氧体负载Cu2O的表征与讨论 20 3.3.1光催化应用 20 3.3.2镍锌铁氧体负载Cu2O的光催化性能 21 3.3.4镍锌铁氧体负载Cu2O的XRD分析 27 第四章 结论 28 致谢 29 参考文献 30  第一章 前言 1.1制备