Mg-8Gd-3Y-0.6Zr合金热压缩过程动态再结晶.PDFVIP

19 12 2009 12 Vol.19 No.12 The Chinese Journal of Nonferrous Metals Dec. 2009 1004-0609(2009)12-2067-07 Mg-8Gd-3Y-0.6Zr 1 1 1, 2 1 1 (1. 410083 2. 421002) Mg-8Gd-3Y-0.6Zr 623~773 K 0.01~1 s−1 Zener-Hollomon (Z) {0001}{10 10} Z ln(Z)28~32 723~773 K Zener-Hollomon TG146.2 A Dynamic recrystallization of Mg-8Gd-3Y-0.6Zr alloy during hot-compression 1 1 1, 2 1 1 ZHANG Xin-ming , ZHOU Nan , LI Li , TANG Chang-ping , DENG Yun-lai (1. School of Materials Science and Engineering, Central South University, Changsha 410083, China; 2. Department of Mechanical Engineering, Hunan Institute of Technology, Hengyang 421002, China) Abstract: The regularity of dynamic recrystallization in Mg-8Gd-3Y-0.6Zr alloy during hot-compression was investigated. For this purpose, the uniaxial compression was conducted at different deformation temperatures (from 623 K to 773 K) and various strain rates (from 0.01 s−1 to 1 s−1). The microstructure and macrotexture after compression were studied by optical microscope (OM), scanning electron microscopy (SEM) and X-ray texture measurement. The results show that the peak stress and the steady-state flow stress become higher with increasing Zener-Hollomon parameter (Z); Increasing deformation temperature or strain rate can weaken the {0001} basal texture and strengthen the {10 10} prismatic texture; the grain size of dynamic recry