北京市成城交大建材有限公司-产品说明书-中英文-2014-07-08.docVIP

PAGE \* MERGEFORMAT 1 PAGE \* MERGEFORMAT 1 CC-AI聚羧酸系高性能减水剂 CC-AI poly carboxylic acid high performance water reducing agent 产品概述Product Introduction CC-AI聚羧酸系高性能减水剂系聚合羧酸梳状接枝共聚物，能在水泥表面形成稳定的立体保护层，产生空间位阻效应，所以具有高分散性和流动度保持性。其减水率可达40%，可制备出高坍落度及大流态混凝土，有极佳的工作性/CC-AI polycarboxylate high performance water reducer is graft copolymer of carboxylic acid polymerization, which can form stable protective layer on the surface of cement where can produce steric hindrance effect, hence it has excellent fluidity retentivity. The water reducer is above 40%, prepared with high slump and flow state in concrete and has excellent workability. 匀质性指标Homogeneity index 项目 Items 指标Specification 项目Items 指标Specification 外观Appearance 淡黄色或棕黄色液体Light yellow or brown liquid PH值pH Value 3-7 比重Proportion 1.02-1.15 缓凝时间Retarding Time 2-5h(也可视实际情整adjust according to the situation) 含固量Solid Content 7-38% 减水率Water Reduction Rate 20-40% 主要技术性能Technology Performance 1、掺量低：通常按总胶凝材料的1.0-3.0%/Low Dosage: In general, according to the cementitious materials of 1.0-3.0%. 2、良好施工性：1-2h可保证坍落度基本无损失，良好保水性粘聚性，便于施工操作/Good Constructability: Good slump retention sustains 1-2h, Good water retention ability and adhesion ability, making concrete have excellent workability. 3、高耐久性：本品可降低砼水胶比，提高砼密实性，抗冻融，抗渗性及耐腐蚀性，并能有效的减少砼体积收缩变形/Good Durability: Reducing the concrete water-binder ratio, improving the density, anti-freezing and anti-permeability and corrosion resistance, reducing the volume shrinkage of concrete. 4、环保性：本产品无氯、低碱，在生产和使用过程中不产生对自然环境的污染/Environmental Products: No chloride, low alkali, no pollution. 应用技术要点Application Technology 1、请遵照《混凝土外加剂应用技术规范》的规定进行施工/Construction Comply with《code for utility technical of concrete admixture》. 2、现场施工中应严格控制掺量/Strictly controlling the dosage during the construction. 3、初用本品或改变水泥品种时，应进行试配，以取得最佳的技术效果和经济效益/The first use of concrete admixture or change the cement type should be tested for reaching the excellent effect of technology and economic benefits. 4、使用时把本品与水同时掺入砼拌合料中即可/It can be