中水回用于循环冷条却水时缓蚀阻垢剂的性能研究.docVIP

——————————————————————————————————————————————— 中水回用于循环冷却水时缓蚀阻垢剂的性能研究 舒 纯1 于 萍2 肖兰芳2 李建梅2 (1. 武汉钢铁集团公司能源动力总厂，武汉 430083; 2. 武汉大学，武汉 430072） 摘 要 本文通过静态法和动态模拟法评价中水用于循环冷却水系统时的缓蚀阻垢剂性能。试验表明，预膜后的试片放入含有12～50mg.L-1 WGS-1:WGS-2=6:1的药剂下运行，其腐蚀速率小于0.04mm.a-1，缓蚀率大于90%，极限浓缩倍率达5.6，满足循环冷却水运行要求。 关键词 循环冷却水 缓蚀剂 缓蚀性能 Study on Performance of Corrosion and Scale Inhibitors Applied in Recirculating Cooling Water of Reclaimed Water Reuse Shu Chun1 Yu Ping2 Xiao Lanfang2 Li Jianmei2 (1. Energy and Power General Factory, Wuhan Iron and Steel Group Corp, Wuhan, 430083; 2. College of Chemistry and Molecule Science, Wuhan University, Wuhan,430072) Abstract Performance of corrosion and scale inhibitors applied in circulating cooling water was evaluated by static method and dynamic simulation method in this paper. The experimental results show that the corrosion rate is less than 0.04mm.a-1，the corrosion inhibition rate is more than 90% and the concentration ratio limited is up to 5.6 when the test coupon was pre-filmed and put in circulating cooling water with 12～50mg.L-1 dosage of corrosion inhibitors WGS-1:WGS-2=6:1. It can meet the use demand of circulating cooling water. Key words circulating cooling water，corrosion inhibitor，corrosion inhibition performance 为了达到国家节水减排、节约能源的要求，武钢综合废水经过污水处理后已用于循环冷却水的补充水，由于该中水中含有较多的杂质离子及循环水的不断浓缩，目前冷却设备的腐蚀问题较为突出。常用方法就是在循环水中添加缓蚀阻垢剂，这样既可以减少金属的腐蚀，又可提高循环水的浓缩倍数达到节约用水的目的。本文主要针对武钢污水处理站的出水水质，通过静态和动态模拟试验，筛选合适的循环冷却水缓蚀阻垢剂，确定最佳的运行参数，以期保证该中水回用于循环冷却水系统时的正常运行。 1 试验部分 1.1 原材料和仪器 材料：Q235碳钢；缓蚀阻垢剂有：WGS-1、WGS-2、WGS-3、WGS-4、WGS-5及WL-1等；分析仪器：DDS-11A型电导率仪、PHS-3C型pH计、EL204电子天平及DRDT型水垢测定仪等。 第八届（2011）中国钢铁年会论文集 1.2 试验用水 试验用水为武钢污水处理站的出水，其水质见表1。 表1 武钢污水处理站出水水质分析 检测项目名称 水质指标 检测项目名称 水质指标 固体溶解物～847 pH 7.10～7.33 甲基橙碱度～1.8 总硬度/mmol.L-1 CODCr /mg.L-1 ～2.15 8.63～18.2 电导率/μ～850 Cl～119.3 Ca2+/mg.L-1(相当于CaCO3～195 酚酞碱度/mmol.L-1 0 －总～0.5 浊度～1.34 油类/mg.L-1 ～1.10 1.3