长输天然气管线的腐蚀与防护.doc

长输天然气管线的腐蚀与防护 陈胜利 兰志刚 宋积文 王在峰 （中海油能源发展股份有限公司北京分公司，北京，100027） 摘要：文章分析了在我国南方天气和地质环境下长输天然气管线的腐蚀与防护技术。针对中国海洋石油某管网公司的长输天然气管道检测了腐蚀状况，并对该长输管线进行了防腐蚀阴保改造，使该段长输管线达到了保护状态，保障长输管线的安全运行。最后，对埋地天然气长输管线的腐蚀与防护技术提出了建议。 关键词：长输管道腐蚀，阴极保护，防腐蚀技术, 埋地管道 中图分类号：TG174 文章标识码：A 文章编号： Protection and Corrosion for Long-distance buried Gas Pipeline Shengli Chen*, Zhigang Lan, Jiwen Song, Zaifeng Wang （Beijing Company of CNOOC Enterprises Co., Beijing, 100027） Abstract: This paper analyzed the corrosion and protection for long-distance buried gas pipeline in south china at climate and geological environment. Corrosion of gas pipeline at company of CNOOC was detected. Cathodic protection was used on long-distance buried gas pipeline, so that safety operation was in pipeline. At last buried gas pipeline corrosion and protection of technical recommendations was proposed. Keywords: Corrosion of Long-distance Gas Pipeline, Cathodic Protection, Anti-corrosion Technology, Buried pipeline 0 前言 目前，石油、天然气资源的输送主要依靠长距离埋地管道来实现，管材一般为普通钢制螺旋焊管。由于长输天然气管道一般采用浅埋地方式铺设[1]，特别是南方气候湿润，地下水位较高和河流众多，埋地穿越地段地形复杂，土壤对管道有着不同程度且很强的腐蚀性，漏损处也不易及时发现，且地下管道的维修要进行大量的土方工程，比新建管线还要费工[2~4]。因此，如何防止长输油气埋地管道的腐蚀破坏，长期以来一直是管道工程中的一个重要环节。 中海油的某管网公司地处南方广东省，铺设管道短短几年就面临着严峻的腐蚀问题。因为广东省气候和地质因素，加上河流众多，使长输管道河流穿越段非 —————————————————————— 联系人：陈胜利，男，1982年生，硕士研究生，防腐工程师， 通讯地址：北京市东三环北路甲2号京信大厦1435室；邮编：100027；电话：010传真：010 Email： HYPERLINK mailto:chenshl2@ chenshl2@ 研究方向：海洋石油天然气工程的腐蚀与防护 常多，造成了严重的腐蚀问题。文中利用多种技术对长输管线进行了无损检测，对管线的整体进行腐蚀评价并提出了防腐蚀改造措施。经过防腐改造后该段管线达到防腐蚀要求，保证了生产安全和天然气的正常输送。 1 埋地长输天然气管道腐蚀因素分析 埋地天然气钢质管道发生腐蚀主要有四大影响因素：即地质环境影响、管道外防腐层效果、钢管材质及制造工艺、输送介质及条件[5]。事实上管道的腐蚀破坏是上述诸因素相互影响的结果。 1.1埋地管道所处的地质环境 埋地管道在工作环境下，受着多种腐蚀，主要腐蚀情况有：土壤腐蚀、细菌腐蚀和杂散电流腐蚀。土壤是具有固、液、气三相的毛细管多孔性的胶质体，土壤的空隙为空气和水所充满，水中含有一定量的盐使土壤具有离子导电性；土壤物理化学性质的不均匀性和金属材质的电化学不均匀性，构成了埋地管道的电化学腐蚀条件，从而会产生土壤腐蚀。在一些缺氧的土壤中有细菌(硫酸盐还原菌)参加了腐蚀过程，细菌的作用是参加电极反应将可溶硫酸盐转化为硫化氢与铁作用，产生细菌腐蚀。 杂散电流是在地下流动的防护系统设计之外对金属管道产生腐蚀破坏作用的电流。杂散电流腐蚀包括直流杂散电流腐蚀和交流杂散电流腐蚀。直流杂散电流腐蚀原理与电解腐蚀类似；交流杂散电流是管道附近高压电力线产生的二次感应交流电叠加在管道腐蚀电化学电池产生的腐蚀，其