准贝氏体组织及新型系列准贝氏体钢.docxVIP

准贝氏体组织及新型系列准贝氏体钢杨延清 陈 彦 准贝氏体组织及新型系列准贝氏体钢 杨延清 陈 彦 康沫狂 (西北工业大学材料科学与工程系, 西安 710072) 摘 要 新型钢中的准贝氏体由贝氏体铁素体和分布其上的残余奥氏体膜组成, 处于贝氏体转变的初期 阶段。 新型准贝氏体钢具有优异的综合力学性能和简单易行的工艺性能, 应用前景广阔。 关键词 准贝氏体钢 相变 性能 M icro struc ture of M e ta Ba in ite an d New M e ta Ba in it ic Stee l Ser ie s Y an g Y an q in g, C h en Y an an d K an g M o k u an g (D ep t. o f M a te r ia ls Sc ience and E ng inee r ing, N o r thw e ste rn Po ly tech n ica l U n ive r sity, X ian 710072) A bstrac t T he m e ta ba in ite in new stee l co n sist s ba in it ic fe r r ite (B F ) and re ta ined au sten ite (A ) th in f ilm s w ith in the B F and fo rm s in the ea r ly stage o f ba in it ic t ran sfo rm a t io n. T he new stee l se r ie s ha s exce llen t com p rehen sive m echan ica l p rop e r t ie s and sim p le p ro ce ssing behav io r w ith w ide app lica t io n in a va r ie ty o f indu st r ia l f ie ld. M a ter ia l In dex M e ta B a in ite S tee l, P h a se T ran sfo rm a t io n, M ech an ica l P rop e r ty 在贝氏体相变理论方面, 进行了大量研究工 作已取得丰硕成果。但对贝氏体转变机制的认识 还存在相互矛盾的两大学派, 即切变机制和扩散 的台阶生长机制1 ～ 4 。尽管如此, 基于对贝氏体组 织的认识, 国内外先后开发了多种贝氏体钢, 具 有明显的工艺优势3 。 然而一般贝氏体钢中, 不 可避免地会出现上贝氏体组织, 使得其力学性能 降低, 尤其是冲击韧度不高, 限制了贝氏体钢的 应用。 通过对贝氏体相变的深入研究, 我们提出了 “准贝氏体”这一概念4 , 并研制成功系列准贝氏 体 钢, 其 综 合 力 学 性 能 超 过 当 前 的 典 型 贝 氏 体 钢、调质钢甚至超高强度钢, 为贝氏体钢研究开 辟了新途径。系列新型准贝氏体钢已成为国家科 技成果重点推广项目5 。 为了避免 BC 的出现, 在贝氏体钢中加入 S i、 A l 等阻碍碳化物析出的合金元素, 使得贝氏体转 变明显分为两个阶段6 。 在贝氏体孕育期内, 过 冷奥氏体形成贫碳区与富碳区, B F 在过冷奥氏 体的贫碳区切变形成, 其间分布着富碳的残余奥 氏体薄膜 (A R ) , 此 时 处 于 贝 氏 体 转 变 的 初 期 阶 段, 此类贝氏体即为准贝氏体。如图 1 所示, 准贝 氏体中的 A R 分为两类: A I R 分布在 B F 条间并与 B F 长轴平行; A | 分布在B F 条内且与B F 长轴约 R 1 准贝氏体的组织特点及贝氏体转变的阶段性 一般的典型上贝氏体是贝氏体铁素体 (B F ) 及在其间分布着平行于其长轴的贝氏体碳化物 (BC ) 的混合体, 典型下贝氏体是 B F 及在其上分 布着与长轴约 55～ 66? 角的 BC 的混合体。由于 碳化物的存在, 不利于对 B F 形成机理的研究。 图 1 准贝氏体组织的两种残余奥氏体膜 F ig. 1 Tw o k ind o f re ta ined au sten ite th in f ilm in m e ta ba in ite 特殊钢第 20 卷·36·呈 15～ 25? 角。 在光学显 特殊钢 第 20 卷 ·36· 呈 15～ 25? 角。 在光学显微镜下, 准贝氏体组织 呈粒状和针状形貌, 冷速慢, 粒状较多, 冷速快, 针状较明显 ( 图 2